Studying the failure of a CFRP sample under static loading by the acoustic-emission and fractography methods

被引：11
|
作者：
Stepanova, L. N. [1 ]
Bataev, V. A. [2 ]
Chernova, V. V. [3 ]
机构：
[1] Chaplygin Siberian Aeronaut Res Inst, Novosibirsk 630051, Russia
[2] Novosibirsk State Tech Univ, Novosibirsk 630073, Russia
[3] Siberian Transport Univ, Novosibirsk 630049, Russia
来源：
RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING | 2017年 / 53卷 / 06期
关键词：
carbon-fiber reinforced plastic (CFRP); sample; acoustic emission; thin section; fractography; exfoliation; fiber; matrix;
D O I：
10.1134/S1061830917060092
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Relationship between the main informative parameters of acoustic-emission (AE) signals recorded during static loading of a CFRP sample and the process of material fracture has been investigated. Clusterization of AE signals by digitized shape has made it possible to locate a zone they originate from. Material was then cut out from this zone to prepare thin sections that were subjected to fractography. Fractography revealed fiber fracture, brittle cracking of the matrix, its exfoliation from the carbon fibers, etc.
引用
收藏
页码：422 / 429
页数：8
相关论文
共 50 条
  • [1] Studying the failure of a CFRP sample under static loading by the acoustic-emission and fractography methods
    L. N. Stepanova
    V. A. Bataev
    V. V. Chernova
    Russian Journal of Nondestructive Testing, 2017, 53 : 422 - 429
  • [2] Acoustic-Emission Testing of Failure in Samples of CFRP Exposed to Static and Heat Loads
    L. N. Stepanova
    V. V. Chernova
    E. S. Petrova
    I. S. Ramazanov
    Russian Journal of Nondestructive Testing, 2018, 54 : 748 - 756
  • [3] Acoustic-Emission Testing of Failure in Samples of CFRP Exposed to Static and Heat Loads
    Stepanova, L. N.
    Chernova, V. V.
    Petrova, E. S.
    Ramazanov, I. S.
    RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING, 2018, 54 (11) : 748 - 756
  • [4] Acoustic-Emission Monitoring of Airframe Failure under Cyclic Loading
    Yu. G. Matvienko
    I. E. Vasil’ev
    D. V. Chernov
    V. A. Pankov
    Russian Journal of Nondestructive Testing, 2019, 55 : 570 - 580
  • [5] Acoustic-Emission Monitoring of Airframe Failure under Cyclic Loading
    Matvienko, Yu. G.
    Vasil'ev, I. E.
    Chernov, D. V.
    Pankov, V. A.
    RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING, 2019, 55 (08) : 570 - 580
  • [6] ACOUSTIC-EMISSION FOR POLYCRYSTALLINE GRAPHITE UNDER COMPRESSIVE LOADING
    IOKA, I
    YODA, S
    KONISHI, T
    CARBON, 1990, 28 (04) : 489 - 495
  • [7] ACOUSTIC-EMISSION FROM CRYSTALS UNDER CONCENTRATED LOADING
    AKCHURIN, MS
    ZLATKIN, AT
    KATZ, MS
    LUBE, EL
    MIKHINA, EY
    REGEL, VR
    FIZIKA TVERDOGO TELA, 1989, 31 (04): : 160 - 166
  • [8] Analysis of variations of the dynamic characteristics of acoustic-emission sources under static loading of metal specimens
    A. L. Bobrov
    Russian Journal of Nondestructive Testing, 2009, 45 : 304 - 309
  • [9] Analysis of Variations of the Dynamic Characteristics of Acoustic-Emission Sources under Static Loading of Metal Specimens
    Bobrov, A. L.
    RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING, 2009, 45 (05) : 304 - 309
  • [10] Acoustic Emission Testing of Early Generation of Defects in CFRP Samples under Static and Thermal Loading
    Stepanova, L. N.
    Chernova, V. V.
    Ramazanov, I. S.
    RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING, 2020, 56 (10) : 784 - 794
12345