Effects of ultrasonic impact treatment on pre-fatigue loaded high-strength steel welded joints

被引：33
|
作者：
Zhang, Hai
Wang, Dongpo [1 ]
Xia, Liqian
Lei, Zhenyu
Li, Yizhe
机构：
[1] Tianjin Key Lab Adv Joining Technol, Tianjin 300072, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2015年 / 80卷
基金：
中国国家自然科学基金;
关键词：
Ultrasonic impact treatment; Pre-fatigue; Fatigue life; Cracks; Finite element analysis; IMPROVEMENT; RESISTANCE;
D O I：
10.1016/j.ijfatigue.2015.06.017
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Comparative fatigue tests were conducted on as-welded, weld toe peened specimens before and after fatigue loading. Fracture surface, residual stress, microstructure and hardness were determined. The test results showed that as the pre-fatigue loading period extended, deeper cracks may have initiated and propagated and the fatigue life improvement decreased. The processes of ultrasonic peening on welded joints with existing cracks were modeled by finite element analysis. The numerical results indicated that the mechanism of UIT improving fatigue performance included two factors: compressive residual stress and the change of crack orientation. Both effects reduced as the crack became deeper. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：278 / 287
页数：10
相关论文
共 50 条
  • [1] The influence of ultrasonic impact treatment on fatigue behaviour of welded joints in high-strength steel
    Galtier A.
    Statnikov E.S.
    Welding in the World, 2004, 48 (5-6) : 61 - 66
  • [2] Fatigue Strength of High-strength Welded Steel Joints
    Leitner, Martin
    Stoschka, Michael
    Ottersböck, Markus
    Simunek, David
    BHM Berg- und Huttenmannische Monatshefte, 2015, 160 (01): : 9 - 14
  • [3] Fatigue Life Improvement of the High Strength Steel Welded Joints by Ultrasonic Impact Peening
    Lago, Jan
    Trsko, Libor
    Jambor, Michal
    Novy, Frantisek
    Bokuvka, Otakar
    Mician, Milos
    Pastorek, Filip
    METALS, 2019, 9 (06)
  • [4] Effects of pre-fatigue damage on mechanical properties of Q690 high-strength steel
    Zhang, Chuntao
    Wang, Ruheng
    Song, Gangbing
    CONSTRUCTION AND BUILDING MATERIALS, 2020, 252
  • [5] Recent results on fatigue strength improvement of high-strength steel welded joints
    Yildirim, Halid Can
    INTERNATIONAL JOURNAL OF FATIGUE, 2017, 101 : 408 - 420
  • [6] Effect of stress ratio on the enhancement of fatigue strength in high performance steel welded joints by ultrasonic impact treatment
    Hiroshi Shimanuki
    Teppei Okawa
    International Journal of Steel Structures, 2013, 13 : 155 - 161
  • [7] Effect of stress ratio on the enhancement of fatigue strength in high performance steel welded joints by ultrasonic impact treatment
    Shimanuki, Hiroshi
    Okawa, Teppei
    INTERNATIONAL JOURNAL OF STEEL STRUCTURES, 2013, 13 (01) : 155 - 161
  • [8] Effect of pre-fatigue on impact tensile properties of laser welded butt joint of high strength steel plates
    Suzuki Motor Co., Takatsuka-cho, Hamamatsu, 432-8611
    不详
    不详
    Zairyo, 2006, 9 (824-830):
  • [9] Effect of ultrasonic impact treatment (UIT) on fatigue strength of welded joints
    Suzuki, T.
    Okawa, T.
    Shimanuki, H.
    Nose, T.
    Ohta, N.
    Suzuki, H.
    Moriai, A.
    RESIDUAL STRESSES IX, 2014, 996 : 736 - +
  • [10] CRACKING OF HIGH-STRENGTH STEEL WELDED JOINTS
    Pancikiewicz, K.
    Zielinska-Lipiec, A.
    Tasak, E.
    ADVANCES IN MATERIALS SCIENCE, 2013, 13 (03): : 76 - 85
12345