Effects of h-BN addition on microstructures and mechanical properties of β-CaSiO3 bioceramics

被引：3

作者：

Pan, Ying ^{[1
,2
]}

Yao, Dongxu ^{[1
]}

Zuo, Kaihui ^{[1
]}

Xia, Yongfeng ^{[1
]}

Yin, Jinwei ^{[1
]}

Liang, Hanqin ^{[1
]}

Zeng, Yuping ^{[1
]}

机构：

[1] Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, Shanghai 200050, Peoples R China

[2] Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China

来源：

JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS | 2016年 / 62卷

基金：

中国国家自然科学基金;

关键词：

beta-CaSiO3; h-BN; Glassy phase; Mechanical properties; Bioceramic; LOW-TEMPERATURE; DIELECTRIC-PROPERTIES; CAO-B2O3-SIO2; GLASS; MAGNETIC-PROPERTIES; CERAMICS; SYSTEM; NANOCOMPOSITE; BIOACTIVITY;

D O I：

10.1016/j.jmbbm.2016.05.014

中图分类号：

R318 [生物医学工程];

学科分类号：

0831 ;

摘要：

The main purpose of this study consists in investigating the effects of h-BN addition on the sinterability of beta-CaSiO3 (beta-CS) bioceramics. beta-CS bioceramics with different contents of h-BN were prepared at the sintering temperature ranging from 800 degrees C to 1100 degrees C. The results showed that h-EN can be successfully used as sintering additive by being oxidized to form low melting point B2O3 related glassy phase and enhanced the flexural strength by the formation of rod-like beta-CS grains. beta-CS bioceramics with 1 we% h-BN sintered at 1000 degrees C revealed flexural strength and fracture toughness of 182.2 MPa and 2.4 MPa m(1/2) respectively, which were much higher than that of pure beta-CS bioceramics (30.2 MPa, 0.53 MPa m(1/2)) fabricated in the same processing condition. (C) 2016 Elsevier Ltd. All rights reserved.

引用

页码：275 / 281

页数：7

共 50 条

[1] Effects of silica sol on the microstructure and mechanical properties of CaSiO3 bioceramics
Pan, Ying
Yin, Jinwei
Yao, Dongxu
Zuo, Kaihui
Xia, Yongfeng
Liang, Hanqin
Zeng, YuPing
MATERIALS SCIENCE AND ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2016, 64 : 336 - 340
[2] The improved mechanical properties of β-CaSiO3 bioceramics with Si3N4 addition
Pan, Ying
Zuo, Kaihui
Yao, Dongxu
Yin, Jinwei
Xie, Yunchuan
Xia, Yongfeng
Liang, Hanqin
Zeng, Yuping
JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 2016, 55 : 120 - 126
[3] The sintering behavior and mechanical properties of CaSiO3 bioceramics with B2O3 addition
Pan, Ying
Yin, Jinwei
Zuo, Kaihui
Yao, Dongxu
Xia, Yongfeng
Liang, Hanqin
Zeng, YuPing
CERAMICS INTERNATIONAL, 2016, 42 (07) : 9222 - 9226
[4] Effects of h-BN on mechanical properties of reaction bonded β-SiAlON/h-BN composites
Li, Yanjun
Ge, Bangzhi
Wu, Zhihong
Xiao, Guoqing
Shi, Zhongqi
Jin, Zhihao
JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 703 : 180 - 187
[5] Dielectric properties and microstructures of CaSiO3 ceramics with B2O3 addition
Wang, Huan-ping
Xu, Shi-qing
Lu, Shui-qin
Zhao, Shi-long
Wang, Bao-ling
CERAMICS INTERNATIONAL, 2009, 35 (07) : 2715 - 2718
[6] SPS fabrication and mechanical properties of β-CaSiO3
Zhao Songjue
Wang Lianjun
Jiang Wan
Chen Lidong
RARE METAL MATERIALS AND ENGINEERING, 2007, 36 : 354 - 356
[7] Preparation and in vitro Properties of CaSiO3/TiO2 Composite Bioceramics
Yu Hui-Xian
Ning Cong-Qin
JOURNAL OF INORGANIC MATERIALS, 2013, 28 (01) : 69 - 73
[8] UHMWPE/CaSiO3 Nanocomposite: Mechanical and Tribological Properties
Danilova, Sakhayana N.
Yarusova, Sofia B.
Kulchin, Yuri N.
Zhevtun, Ivan G.
Buravlev, Igor Yu.
Okhlopkova, Aitalina A.
Gordienko, Pavel S.
Subbotin, Evgeniy P.
POLYMERS, 2021, 13 (04) : 1 - 17
[9] Effects of h-BN content on properties of Ni-Cr/h-BN composite
Xiao-feng Wei
Ri-chu Wang
Yan Feng
Chao-qun Peng
Xue-wei Zhu
Journal of Central South University, 2011, 18 : 1334 - 1339
[10] Effects of h-BN content on properties of Ni-Cr/h-BN composite
Wei Xiao-feng
Wang Ri-chu
Feng Yan
Peng Chao-qun
Zhu Xue-wei
JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2011, 18 (05): : 1334 - 1339

← 1 2 3 4 5 →