Thermal and photochemical reactivity of oxygen atoms on gold nanocluster surfaces

Reduction of oxidized gold nanoclusters by exposures to foreign gases and irradiation of UV photons has been investigated using X-ray photoelectron spectroscopy. Gold nanoclusters with narrow size distributions protected by alkanethiolate ligands were deposited on a TiO2(1 1 0) surface with dip coating. Oxygen plasma etching was used for removal of alkanethiolate ligands and oxidization of gold clusters. The oxidized gold clusters were exposed to CO, C2H2, C2H4, H-2, and hydrogen atoms. Although, C2H4 and H-2 did not show any indications of reduction of oxidized gold clusters, CO, C2H2, and hydrogen atoms reduced the oxides on gold cluster surfaces. Among them, hydrogen atoms were most effective for reduction. Irradiation of UV photons around 400 nm could also reduce the oxidized gold clusters. The photochemical reduction mechanism was proposed as follows. The photo-reduction was initiated by electronic excitation of gold clusters and oxygen atoms activated reacted with carbon atoms at the surfaces of gold clusters. Carbon species were likely absorbed in gold clusters or remained at the boundaries between gold clusters when gold clusters agglomerated during oxygen plasma exposures. As the photochemical reduction progressed, carbon atoms segregated to the surfaces of gold clusters. (c) 2007 Elsevier B.V. All rights reserved.