A Comprehensive Approach of Eucalyptus globulus Acid Sulfite Pretreatment for Enzymatic Hydrolysis

The effect of different acid sulfite pretreatment conditions on released components in the hydrolysates and the pretreated solid residues' response to enzymatic hydrolysis for Eucalyptus globulus chips was investigated. Sodium bisulfite (0-15%), and sulfuric acid (0-5%) were used to pretreat chips at 170 degrees C and 190 degrees C, for as long as 30 min. The hydrolysates were analyzed through high-performance liquid chromatography (HPLC) and spectrophotometry. Overall porosity and pores larger than 2.65 nm (size of a typical cellulase) on the solid residues were estimated using glucose and two dextrans with different hydrodynamic radii as probes. The external specific surface area was analyzed by dynamic light scattering. The solid residues underwent enzymatic hydrolysis with an enzymatic cocktail. Very high (84-95%) carbohydrate conversion was achieved for either an extensively delignified biomass or a biomass with very high content of sulfonated residual lignin (23.4%), since internal porosity enables enzymes accessibility. At least 5% sodium bisulfite and 1% sulfuric acid was required to attain a carbohydrate release above 90% in the enzymatic hydrolysis. Results suggest that the presence of sulfonated lignin does not impair the enzymatic hydrolysis rate and extent. The increase of pretreatment temperature had a positive effect mainly on the initial rate of carbohydrates release in the enzymatic hydrolysis. The increase of the wood material dimensions from pins to conventional chips significantly decreased the hemicellulose removal in acid sulfite pretreatment but had a small effect on the enzymatic yield.