Enhanced dielectric and piezoelectric properties in potassium sodium niobate/polyvinylidene fluoride composites using nano-silicon carbide as an additive

Piezoelectric materials are an indispensable part of modern life. Yet the existing environmental issues with conventional lead-based piezoelectrics has motivated scientist to develop novel substitutes including lead-free piezoelectric polymer composites. Following this path, the present research has focused on the fabrication of ternary composites of Polyvinylidene fluoride (PVDF)/Potassium Sodium Niobate (KNN)/nano-Silicon carbide (SiC) via hot compression molding and studying the effect of additives on the PVDF structure and the electrical properties of the composite. The obtained scanning electron micrographs and density measurements showed that the fabrication method provided dense samples. The activated polarization phenomena in the prepared samples enhanced dielectric permittivity and dielectric loss at a constant frequency with increasing KNN and SiC contents. Besides the expected dipole polarization, the presence of interfaces in the composites gave rise to the Maxwell-Wagner-Sillars effect and its corresponding polarization phenomenon. The semiconductive nature of SiC also promoted space charge polarization. However, these properties were frequency-dependent because the first two polarization mechanisms are deactivated at high frequencies. XRD patterns showed that SiC addition can alter the primary crystalline structure of PVDF and promote beta-phase formation in the poled samples. Piezoelectric measurements confirmed the significant role of SiC addition to PVDF-KNN composites. The most significant increase in the piezoelectric properties was observed in PVDF-60KNN-1SiC, with a 183% increase in d33 value. The PVDF-80KNN-1SiC had the highest d33 value of 30.5 pC/N. It also had the best piezoelectric voltage coefficient and hence the highest figure of merit. Higher SiC contents restrict the efficiency of poling by forming a conductive path across the sample which would deteriorate the piezoelectric performance of the material. The present findings show that PVDF-KNN-SiC composites can be considered as a potential flexible piezoelectric material for future applications.