Microstructure and texture evolution during annealing of Ti-6Al-4V alloy

被引：9
|
作者：
Debta, M. K. [1 ]
Bishoyi, B. D. [1 ]
Sabat, R. K. [2 ]
Muhammad, W. [3 ]
Sahoo, S. K. [1 ]
机构：
[1] NIT Rourkela, Dept Met & Mat Engn, Rourkela 769008, India
[2] IIT Bhubaneswar, Sch Minerals Met & Mat Engn, Argul, India
[3] Univ Waterloo, Dept Mech & Mechatron Engn, Waterloo, ON, Canada
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2020年 / 36卷 / 04期
关键词：
Ti-6Al-4V; Rolling; Annealing; Recrystallization; Microstructure; Texture; EBSD; XRD; TITANIUM; GLOBULARIZATION;
D O I：
10.1080/02670836.2019.1706816
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Ti-6Al-4V plates were subjected to warm rolling at 600 degrees C up to 85% reduction in thickness followed by annealing at 850 degrees C for different soak periods. It was observed that the 'beta' grains were prevalent along the grain boundaries and at the triple junctions of 'alpha' grains. The samples were found to be fully recrystallised after 30 min of annealing time. Further, globularizarion of 'alpha' grains was observed during the progress of annealing. The recrystallisation mechanism was identified to be through sub-grain formation and its growth. A dominant near basal texture, i.e. (10 (1) over bar7) <70<(7)over bar>(2) over bar> was observed in the samples after annealing.
引用
收藏
页码：417 / 424
页数：8
相关论文
共 50 条
  • [1] Early Stages of Microstructure and Texture Evolution during Beta Annealing of Ti-6Al-4V
    A. L. Pilchak
    G. A. Sargent
    S. L. Semiatin
    [J]. Metallurgical and Materials Transactions A, 2018, 49 : 908 - 919
  • [2] Early Stages of Microstructure and Texture Evolution during Beta Annealing of Ti-6Al-4V
    Pilchak, A. L.
    Sargent, G. A.
    Semiatin, S. L.
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2018, 49A (03): : 908 - 919
  • [3] Mechanism of texture and microstructure evolution during warm rolling of Ti-6Al-4V alloy
    Sabat, R. K.
    Pavan, M. V. S. S. D. S. Surya
    Aakash, D. S.
    Kumar, M.
    Sahoo, S. K.
    [J]. PHILOSOPHICAL MAGAZINE, 2018, 98 (28) : 2562 - 2581
  • [4] Microstructure and texture evolution during solidification processing of Ti-6Al-4V
    Kobryn, PA
    Semiatin, SL
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 135 (2-3) : 330 - 339
  • [5] Microstructure and Texture Evolution during β processing of Hypoeutectic Boron Modified Ti-6Al-4V Alloy
    Roy, Shibayan
    Suwas, Satyam
    Tamirisakandala, S.
    Srinivasan, R.
    Miracle, D. B.
    [J]. TI-2011: PROCEEDINGS OF THE 12TH WORLD CONFERENCE ON TITANIUM, VOL I, 2012, : 689 - 693
  • [6] Microstructure and Texture Evolution During Symmetric and Asymmetric Rolling of a Martensitic Ti-6Al-4V Alloy
    Qi Chao
    Peter D. Hodgson
    Hossein Beladi
    [J]. Metallurgical and Materials Transactions A, 2016, 47 : 531 - 545
  • [7] Microstructure and Texture Evolution During Symmetric and Asymmetric Rolling of a Martensitic Ti-6Al-4V Alloy
    Chao, Qi
    Hodgson, Peter D.
    Beladi, Hossein
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2016, 47A (01): : 531 - 545
  • [8] The Evolution of Microstructure of Ti-6Al-4V Alloy during Water Cooling
    Li, Jiu-Zhou
    Yu, Huan-Huan
    Li, Zhuang
    Wang, Shuai
    Yu, Tao
    Li, Zhao-Hua
    [J]. PROCEEDINGS OF THE 2015 INTERNATIONAL CONFERENCE ON MATERIAL SCIENCE AND APPLICATIONS (ICMSA 2015), 2015, 3 : 897 - 901
  • [9] Microstructure evolution of Ti-6Al-4V alloy during superplastic deformation
    Wang, Min
    Lin, Chengxiao
    [J]. Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2012, 41 (07): : 1176 - 1180
  • [10] Microstructure Evolution of Ti-6Al-4V Alloy during Superplastic Deformation
    Wang Min
    Lin Chengxiao
    [J]. RARE METAL MATERIALS AND ENGINEERING, 2012, 41 (07) : 1176 - 1180
12345