Mechanical and barrier properties of ternary nanocomposite films based on polycarbonate/amorphous polyamide blends modified with a nanoclay

Ternary polycarbonate (PC)/amorphous polyamide-nanoclay (naPA) nanocomposite (PC/naPA) films were obtained by melt mixing and drawing, and the effects of the naPA content and the draw ratio (DR) on the structure, morphology and mechanical and barrier properties were studied. Despite the presence of nanoclay, the films exhibited a negligible roughness and the excellent optical properties of PC and amorphous polyamide (aPA). The dispersed naPA phase was pure and small, indicating compatibility. The naPA did not hinder the drawing ability of PC. At low DRs the dispersed phase was elongated and oriented along the machine direction (extrusion flow direction), but at high DRs, it fibrillated due to the higher non-isothermal elongational flow induced by drawing. The laminar structure of the nanoclay allowed the films to be reinforced both in the machine and the transverse directions. The oxygen permeability of PC was reduced by 42% in the nanocomposite with 25% of naPA, and dropped further with the DR, which is attributed to the increased tortuosity of the oxygen path induced by fibrillation. Copyright (c) 2015 John Wiley & Sons, Ltd.