Structure and microstructure of EB-PVD yttria thin films grown on Si (111) substrate

Structure and microstructure of yttria thin films grown by electron beam physical vapour deposition on a stationary Si (111) substrate at room temperature (RT), 500 degrees and 700 degrees C, were investigated by the grazing-incidence X-ray diffraction and scanning electron microscopy, respectively. X-ray photoelectron spectroscopy provided information on the surface contamination from the atmosphere and the oxidation state. A strong effect of the deposition temperature and the vapour flux incidence angle was found. The film deposited at RT is polycrystalline with very fine grains of the body-centered cubic (bcc) crystallographic symmetry. An increase of deposition temperature results in a rapid growth of bcc grains with an improved crystalline structure. Moreover, the based-centered monoclinic phase appears for the deposition temperature of 700 degrees C. Preferred grain orientation (texture) with two main components, (400) and (622), was observed in the films deposited at 500 degrees C whereas no texture was found for 700 degrees C. The microstructure exhibits the columnar feather-like structure of different degrees of perfection which can be explained by the shadowing effects caused by an oblique vapour flux incidence angle. Surface morphology of the films is governed by a combination of the triangular and four-sided (square) columns. All films were found to be dense with a little porosity between the columns. (C) 2010 Elsevier Ltd. All rights reserved.