Effects of Processing Residual Stresses on Fatigue Crack Growth Behavior of Structural Materials: Experimental Approaches and Microstructural Mechanisms

Fatigue crack growth mechanisms of long cracks through fields with low and high residual stresses were investigated for a common structural aluminum alloy, 6061-T61. Bulk processing residual stresses were introduced in the material by quenching during heat treatment. Compact tension (CT) specimens were fatigue crack growth (FCG) tested at varying stress ratios to capture the closure and K (max) effects. The changes in fatigue crack growth mechanisms at the microstructural scale are correlated to closure, stress ratio, and plasticity, which are all dependent on residual stress. A dual-parameter Delta K-K (max) approach, which includes corrections for crack closure and residual stresses, is used uniquely to connect fatigue crack growth mechanisms at the microstructural scale with changes in crack growth rates at various stress ratios for low- and high-residual-stress conditions. The methods and tools proposed in this study can be used to optimize existing materials and processes as well as to develop new materials and processes for FCG limited structural applications.