Preparation and swelling behavior of partially hydrolyzed polyacrylamide nanocomposite hydrogels in electrolyte solutions

In this research, nanocomposite hydrogels were prepared by cross-linking of partially hydrolyzed polyacrylamide/sodium montmorillonite aqueous solutions with chromium triacetate. The gelation process and influence of nanoclay content and salt concentration on swelling behavior were investigated. Study of gelation behavior using dynamic rheometry method showed that increasing the nanoclay content decreases the storage modulus, due to the partial adsorption of polymer chains onto the clay surface and ionic interaction between negative layers of sodium montmorillonite and Cr.(3+) By increasing the cross-linker concentration of the gelation system, the viscous energy dissipation properties of the nanocomposite gel decreases. Swelling ratio of the nanocomposite gels in distilled water decreased as the concentration of the nanoclay increased. However, nanocomposite gels showed lower salt sensitivity in electrolyte media compared with unfilled gels.