Microstructure development and properties of HSS-based self-lubrication composites

被引:2
|
作者
Wang, Yanjun [1 ]
Wang, Bin [1 ]
Yang, Liying [1 ]
Wang, Shouren [1 ]
机构
[1] Univ Jinan, Sch Mech Engn, Jinan, Peoples R China
关键词
Microstructure; Self lubrication; Porosity; High speed steel;
D O I
10.4028/www.scientific.net/AMR.217-218.625
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
High speed steel based ceramic preforms with three-dimensionally interpenetrated micropores were fabricated using the mixture of TiH2, CaCO3 and stearic acid as pore-forming agent. A self-made vacuum high pressure infiltration furnace was used to infiltrate the preforms with Pb-Sn based solid lubricants to create almost fully dense self-lubrication composites. The microstructure and properties of HSS-based self-lubrication composites were investigated as a function of sintered porosity. A quantitative analysis of microstructure was correlated with crushing strength microhardness and wear rate to understand the influence of pore size, shape and distribution on mechanical and tribological behavior. Crushing strength and microhardness decreased with an increase in porosity. Meanwhile the decrease in microhardness with increasing porosity was slightly. The friction coefficient of HSS-based self-lubrication composites decreased with increasing the volume fraction of lubricant due to the self-lubrication and unique micropore structure. Within the range of lubricant volume fraction from 0% to 14%, the wear rate of the composites decreased steadily with the increase of lubricant content in the composites. Micropore structure and lubricant volume fraction play an important role in determining wear resistance of the composites whereas the measured bulk properties seem to be of minor importance.
引用
收藏
页码:625 / 630
页数:6
相关论文
共 50 条
  • [1] Fabrication and tribological properties of HSS-based self-lubrication composites with an interpenetrating network
    Wang, Yanjun
    Liu, Zuomin
    Wang, Shouren
    Yang, Liying
    LUBRICATION SCIENCE, 2010, 22 (10) : 453 - 463
  • [2] Mechanical and Tribological Properties of TiC-Reinforced HSS-Based Composites with an Interpenetrating Network for High Temperature Self-Lubrication Applications
    Wang, Yanjun
    Liu, Zuomin
    ADVANCED TRIBOLOGY, 2009, : 32 - 37
  • [3] Self-lubrication and tribological properties of polymer composites containing lubricant
    Lee, Sung-Jun
    Kim, Gang-Min
    Kim, Chang-Lae
    RSC ADVANCES, 2023, 13 (06) : 3541 - 3551
  • [4] SELF-LUBRICATION MECHANISMS IN POLYMER COMPOSITES
    SVIRIDYONOK, AI
    TRIBOLOGY INTERNATIONAL, 1991, 24 (01) : 37 - 43
  • [5] Microstructure and tribological property of self-lubrication CBN abrasive composites containing molybdenum disulfide
    Zhao, Biao
    Ding, Wenfeng
    Kuang, Weijie
    Fu, Yucan
    INDUSTRIAL LUBRICATION AND TRIBOLOGY, 2019, 71 (05) : 712 - 717
  • [6] Microstructure of metal-based solid self-lubrication coating by laser cladding
    State Key Lab, Plastic Forming Simulation and Die and Mould Technology Department, Huazhong University of Science and Technology, Wuhan 430074, China
    Zhongguo Jixie Gongcheng, 2006, 19 (2084-2088):
  • [7] High strength and self-lubrication graphite/SiC composites
    Xue, Rong
    Su, Peng
    Wang, Jiping
    Xie, Wenqi
    Xia, Hongyan
    Xiao, Zhichao
    CERAMICS INTERNATIONAL, 2024, 50 (20) : 39398 - 39405
  • [9] Preparation and tribological properties of carbon fiber/epoxy resin vascular self-lubrication composites
    Cui J.
    Zhang J.
    Mu B.
    Guo J.
    Liu H.
    Yang B.
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 2019, 36 (09): : 2023 - 2030
  • [10] Self-lubrication and tribological properties of SBA-15 as smart microcontainer and resin composites
    Sun, Yiming
    Ren, Yilong
    Zhu, Lina
    Si, Lina
    Kang, Jiajie
    Xie, Guoxin
    POLYMER COMPOSITES, 2022, 43 (11) : 7967 - 7976