High-temperature inhibitor of steel corrosion in sulfuric acid solutions

被引：10
|
作者：
Avdeev, Ya. G. [1 ]
Belinskii, P. A. [2 ]
Kuznetsov, Yu. I. [1 ]
Zel, O. O. [1 ]
机构：
[1] Russian Acad Sci, Frumkin Inst Phys Chem & Electrochem, Moscow, Russia
[2] Tsiolkovskii State Pedag Univ, Kaluga, Russia
来源：
PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES | 2010年 / 46卷 / 07期
关键词：
acid corrosion; corrosion inhibitors; acid etching of steel; high-temperature inhibitors;
D O I：
10.1134/S2070205110070087
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
A new high-temperature (up to 140A degrees C) inhibitor of steel corrosion in sulfuric acid, IFKhAN-92, that yields Z = 99% at a content of at least 1 wt % was developed. To enhance the protective effect of IFKhAN-92 at an elevated temperature, KI additions may be used. IFKhAN-92 was shown to be effective in hindering electrode reactions on steel. The high efficiency of this catalyst in H(2)SO(4) solutions is most likely conditioned by the specific adsorption of IFKhAN-92 molecules on a metal surface.
引用
收藏
页码：782 / 787
页数：6
相关论文
共 50 条
  • [1] High-temperature inhibitor of steel corrosion in sulfuric acid solutions
    Ya. G. Avdeev
    P. A. Belinskii
    Yu. I. Kuznetsov
    O. O. Zel’
    Protection of Metals and Physical Chemistry of Surfaces, 2010, 46 : 782 - 787
  • [2] Inhibitor Protection of Steels in Solutions of Sulfuric Acid under High-Temperature Corrosion (up to 200°C)
    Ya. G. Avdeev
    D. S. Kuznetsov
    S. V. Oleinik
    Protection of Metals and Physical Chemistry of Surfaces, 2018, 54 : 1305 - 1311
  • [3] Inhibitor Protection of Steels in Solutions of Sulfuric Acid under High-Temperature Corrosion (up to 200°C)
    Avdeev, Ya. G.
    Kuznetsov, D. S.
    Oleinik, S. V.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2018, 54 (07) : 1305 - 1311
  • [4] Corrosion inhibition in 2.0 M sulfuric acid solutions of high strength maraging steel by aminophenyl tetrazole as a corrosion inhibitor
    Sherif, El-Sayed M.
    APPLIED SURFACE SCIENCE, 2014, 292 : 190 - 196
  • [5] Erosion-corrosion resistance of various stainless steel grades in high-temperature sulfuric acid solution
    Lindgren, M.
    Siljander, S.
    Suihkonen, R.
    Pohjanne, P.
    Vuorinen, J.
    WEAR, 2016, 364 : 10 - 21
  • [6] NITRIC ACID - A CORROSION INHIBITOR FOR CARBON STEEL IN SULFURIC ACID
    MILLER, RF
    RHODES, PR
    MATERIALS PROTECTION AND PERFORMANCE, 1970, 9 (10): : 33 - &
  • [7] NITRIC ACID AS A CORROSION INHIBITOR FOR CARBON STEEL IN SULFURIC ACID
    MILLER, RF
    RHODES, PR
    MATERIALS PROTECTION, 1969, 8 (12): : 44 - &
  • [8] Metoprolol: New and Efficient Corrosion Inhibitor for Mild Steel in Hydrochloric and Sulfuric Acid Solutions
    Mohammadinejad, Fatemeh
    Hosseini, Seyyed Mohammad Ali
    Zandi, Mehdi Shahidi
    Bahrami, Mohammad Javad
    Golshani, Zahra
    ACTA CHIMICA SLOVENICA, 2020, 67 (03) : 710 - 719
  • [9] CORROSION OF STEEL IN SOLUTIONS OF SULFURIC ACID IN DIMETHYLSULFOXIDE.
    Gerasyutina, L.I.
    Brynza, A.P.
    Fedash, V.P.
    Zerkal', L.V.
    Protection of Metals (English translation of Zaschita Metallov), 1985, 21 (06): : 766 - 767
  • [10] CORROSION OF STEEL IN SOLUTIONS OF SULFURIC-ACID IN DIMETHYLSULFOXIDE
    GERASYUTINA, LI
    BRYNZA, AP
    FEDASH, VP
    ZERKAL, LV
    PROTECTION OF METALS, 1985, 21 (06): : 766 - 767
12345