Microstructure and Mechanical Properties of Wire Arc Additively Manufactured MoNbTaWTi High Entropy Alloys

High-temperature resistant high-entropy alloys (HEAs) have attracted extensive attention due to their excellent thermodynamic stability and mechanical properties, especially at high temperatures. However, a highly effective method for large-size HEAs is still desirable but challengeable. This research reported a facile yet effective strategy for MoNbTaWTi HEAs via in-situ wire arc additive manufacturing (WAAM). The wire was MoNbTaWTi cable-type welding wire (CTWW) consisting of one center wire and seven twisted peripheral wires. Then, additive manufacturing of MoNbTaWTi high entropy alloys (HEAs) was accomplished, and various analytical techniques studied the microstructures and mechanical properties of the overlaying formed layers. X-ray diffraction showed the overlaying formed layers to contain a single disordered BCC solid solution phase with high-temperature structural stability. In addition, the single-phase BCC structure was maintained from 0 to 1400 degrees C. The bottom of the overlaying formed layers was made of columnar cellular structure, and the upper part resembled "cauliflower-like" fine dendrite and equiaxed crystal structure. The hardness of the overlaying formed layers averaged 533 HV0.2 at room temperature. At 1000 degrees C, the hardness was around 110 HV1, close to the value of Inconel 718 alloy (125 HV1). The compressive strength of the overlaying formed alloy layers displayed no sensitivity towards change in temperature from 500 to 1000 degrees C. As the temperature rose from 500 to 1000 degrees C, the compressive strength changed from 629 to 602 MPa, equivalent to only a 27 MPa decrease. The latter was much higher than the strength of Inconel 718 alloy at the same temperature (200 MPa).