Corrosion Behavior of low-carbon steel in tap water treated with permanent magnetic field

被引：23
|
作者：
Bikul'chyus, G [1 ]
Ruchinskene, A [1 ]
Deninis, V [1 ]
机构：
[1] Inst Chem, LT-2600 Vilnius, Lithuania
来源：
PROTECTION OF METALS | 2003年 / 39卷 / 05期
关键词：
Magnetic Field; Inorganic Chemistry; Corrosion Rate; Test Temperature; Corrosion Behavior;
D O I：
10.1023/A:1025890601669
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The corrosion behavior of low-carbon steel in tap water treated with permanent magnetic field (0.05 T) was studied by both gravimetric and electrochemical methods. In the course of 2-h-long experiments, a circulatory flow of water, which was heated to 40 or 70degreesC, passed through magnetic field at a velocity of 0.15 m/s. It was found that the magnetic treatment of water decreases the corrosion rate of steel by 14% on the average, no matter what is the test temperature.
引用
收藏
页码：443 / 447
页数：5
相关论文
共 50 条
  • [1] Corrosion Behavior of Low-Carbon Steel in Tap Water Treated with Permanent Magnetic Field
    G. Bikul'chyus
    A. Ruchinskene
    V. Deninis
    [J]. Protection of Metals, 2003, 39 : 443 - 447
  • [2] Elevation of the Reliability of Corrosion Monitoring of Low-Carbon Steel in Tap Water
    R. Yu. Herasymenko
    H. S. Vasyl’ev
    Yu. S. Herasymenko
    [J]. Materials Science, 2017, 53 : 337 - 342
  • [3] Elevation of the Reliability of Corrosion Monitoring of Low-Carbon Steel in Tap Water
    Herasymenko, R. Yu.
    Vasyl'ev, H. S.
    Herasymenko, Yu. S.
    [J]. MATERIALS SCIENCE, 2017, 53 (03) : 337 - 342
  • [4] CORROSION BEHAVIOR OF BORONIZED LOW-CARBON STEEL
    TSIPAS, DN
    NOGUERA, H
    RUS, J
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 1987, 18 (03) : 295 - 303
  • [5] Effects of Stress on Pitting Corrosion Behavior of Low-carbon steel
    Cao, Huaixiang
    Zhang, Hao
    Qiu, Xingqi
    [J]. PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2013, VOL 6A: MATERIALS AND FABRICATION, 2014,
  • [6] Effects of Cr, Cu, Ni and Ca on the corrosion behavior of low carbon steel in synthetic tap water
    Choi, YS
    Shim, JJ
    Kim, JG
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2005, 391 (1-2) : 162 - 169
  • [7] Corrosion Behavior of a Low-Carbon Steel in Simulated Marine Splash Zone
    Huan-Huan Wang
    Min Du
    [J]. Acta Metallurgica Sinica(English Letters), 2017, 30 (06) : 585 - 593
  • [8] Effects of corrosion pits on the combined hardening behavior of low-carbon steel
    Wang, Youde
    Zhou, Xiaodong
    Kong, Zhengyi
    Xu, Shanhua
    [J]. CONSTRUCTION AND BUILDING MATERIALS, 2024, 447
  • [9] Corrosion Behavior of a Low-Carbon Steel in Simulated Marine Splash Zone
    Wang, Huan-Huan
    Du, Min
    [J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2017, 30 (06) : 585 - 593
  • [10] BEHAVIOR AND INHIBITION OF PITTING CORROSION OF LOW-CARBON STEEL IN ALKALINE MEDIA
    KHEDR, MGA
    ELWAHAB, FMA
    ELHALEEM, SMA
    [J]. BULLETIN DE LA SOCIETE CHIMIQUE DE FRANCE PARTIE I-PHYSICOCHIMIE DES SYSTEMES LIQUIDES ELECTROCHIMIE CATALYSE GENIE CHIMIQUE, 1983, (11-1): : 273 - 277
12345