Effect of Ordinary Portland Cement and Water Glass on the Properties of Alkali Activated Fly Ash Concrete

被引：4

作者：

Bocullo, Vytautas ^{[1
]}

Vaiciukyniene, Danute ^{[1
]}

Gecys, Ramunas ^{[1
]}

Dauksys, Mindaugas ^{[1
]}

机构：

[1] Kaunas Univ Technol, Fac Civil Engn & Architecture, Studentu G 48, LT-51367 Kaunas, Lithuania

来源：

MINERALS | 2020年 / 10卷 / 01期

关键词：

alkali-activated concrete; fly ash; durability; compressive strength; ordinary Portland cement; industrial waste; GEOPOLYMER CONCRETE; SILICA REACTION; SLAG; STRENGTH; OPC;

D O I：

10.3390/min10010040

中图分类号：

P3 [地球物理学]; P59 [地球化学];

学科分类号：

0708 ; 070902 ;

摘要：

This research presents the influence of ordinary Portland cement (OPC) and/or water glass addition on fly ash alkali-activated mortar and concrete. The results show that fly ash (FA) concrete activated with a NaOH solution and water glass mixture had better resistance to freeze and thaw, carbonation, alkali-silica reaction (ASR) and developed higher compressive strength and static elastic modulus compared with the FA concrete activated only with an NaOH solution. The addition of OPC contributes to the development of a denser microstructure of alkali activated concrete (AAC) samples. In the presence of water glass and OPC, the compressive strength (52.60 MPa) of the samples increased more than two times as compared with the reference sample (21.36 MPa) without OPC and water glass. The combination of OPC and water glass showed the increased strength and enhanced durability of AAC. The samples were more resistant to freeze and thaw, ASR, and carbonation.

引用

页数：10

共 50 条

[1] Drying shrinkage of alkali-activated slag and fly ash concrete; A comparative study with ordinary Portland cement concrete
Li, Zhenming
Liu, Jiahua
Ye, Guang
[J]. Heron, 2019, 64 (1-2): : 149 - 163
[2] Investigation of engineering properties of normal and high strength fly ash based geopolymer and alkali-activated slag concrete compared to ordinary Portland cement concrete
Farhan, Nabeel A.
Sheikh, M. Neaz
Hadi, Muhammad N. S.
[J]. CONSTRUCTION AND BUILDING MATERIALS, 2019, 196 : 26 - 42
[3] The suitability for using glass and fly ash in Portland cement concrete
Tuncan, M
Karasu, B
Yalcin, M
[J]. PROCEEDINGS OF THE ELEVENTH (2001) INTERNATIONAL OFFSHORE AND POLAR ENGINEERING CONFERENCE, VOL IV, 2001, : 146 - 152
[4] Fracture properties of alkali-activated slag and ordinary Portland cement concrete and mortar
Ding, Yao
Dai, Jian-Guo
Shi, Cai-Jun
[J]. CONSTRUCTION AND BUILDING MATERIALS, 2018, 165 : 310 - 320
[5] ALKALI-ACTIVATED FLY ASH CONCRETE (CONCRETE WITHOUT CEMENT)
Mikoc, Miroslav
Bjelobrk, Ivan
Korajac, Josip
[J]. TEHNICKI VJESNIK-TECHNICAL GAZETTE, 2011, 18 (01): : 99 - 102
[6] The Effect of Composition on the Mechanical Properties of Alkali-activated Fly Ash-Portland Cement Binary System
Liu, Jun
Fu, Jinyu
Liu, Runqing
Yang, Yuanquan
[J]. PROCEEDINGS OF THE 2016 INTERNATIONAL CONFERENCE ON ARCHITECTURAL ENGINEERING AND CIVIL ENGINEERING, 2016, 72 : 140 - 143
[7] ASR Potentials of glass aggregates in water-glass activated fly ash and Portland cement mortars
Xie, Z
Xiang, W
Xi, Y
[J]. JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2003, 15 (01) : 67 - 74
[8] PROPERTIES AND USE OF FLY ASH IN PORTLAND CEMENT CONCRETE.
Lane, R.O.
Best, J.F.
[J]. Concrete International, 1982, 4 (07) : 81 - 92
[9] PREDICTIONS OF EFFECT OF FLY ASH IN PORTLAND CEMENT MORTAR AND CONCRETE
MINNICK, LJ
WEBSTER, WC
PURDY, EJ
[J]. JOURNAL OF MATERIALS, 1971, 6 (01): : 163 - &
[10] Effects of curing conditions on properties of ternary (ordinary portland cement/fly ash/silica fume) concrete
[J]. ACI Mater J, 1 (49-58):

← 1 2 3 4 5 →