Study of effect of boric acid on Zn-Co alloy electrodeposition from acid baths and on composition, morphology and structure of deposit

被引：11
|
作者：
Karahan, I. H. [1 ]
Cetinkara, H. A. [1 ]
机构：
[1] Univ Mustafa Kemal, Dept Phys, Fac Art & Sci, Antakya, Turkey
来源：
TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING | 2011年 / 89卷 / 02期
关键词：
Electrodeposition; Zn-Co alloy; Corrosion; Boric acid; X-ray diffraction; ZINC-COBALT ALLOY; CORROSION BEHAVIOR; ALKALINE BATH; CHLORIDE BATH; PULSE; COUMARIN; COATINGS; AGENTS;
D O I：
10.1179/174591911X12968393517774
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
The effect of boric acid as additive in electrodeposition of Zn-Co alloy coatings from an acidic sulphate electrolyte containing NH4Cl, Na2SO4 and citric acid Na3C6H5O7, at ambient temperature, without agitation has been investigated. The deposition process was investigated by cyclic voltammetry. It was found that the current density first decreased and then increased, due to adsorption of a boric acid complex and/or changes in the morphology, but the initial deposition potential was not affected. The addition of boric acid to the bath led to the formation of improved Zn-Co deposits, composed of coalesced globular fine grains smaller than similar to 2 mu m in diameter. Also, all of the Zn-Co deposits studied consisted of eta phases. The Co content in the Zn-Co deposits produced in the presence of boric acid increased from 2.5 to 4.3 wt-%. It is suggested that Zn-Co deposits produced in the bath containing 60 g L-1 boric acid probably offer sacrificial protection to the steel substrate.
引用
收藏
页码：99 / 103
页数：5
相关论文
共 50 条
  • [1] Study of the effect of mannitol on ZnNi alloy electrodeposition from acid baths and on the morphology, composition, and structure of the deposit
    E. M. de Oliveira
    I. A. Carlos
    Journal of Applied Electrochemistry, 2009, 39 : 1849 - 1856
  • [2] Study of the effect of mannitol on ZnNi alloy electrodeposition from acid baths and on the morphology, composition, and structure of the deposit
    de Oliveira, E. M.
    Carlos, I. A.
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 2009, 39 (10) : 1849 - 1856
  • [3] Effect of benzylideneacetone on the electrodeposition mechanism of Zn-Co alloy
    Trejo, G
    Ortega, R
    Meas, Y
    Chainet, E
    Ozil, P
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 2003, 33 (05) : 373 - 379
  • [4] Effect of benzylideneacetone on the electrodeposition mechanism of Zn-Co alloy
    Trejo, G., 1600, Kluwer Academic Publishers (33):
  • [5] THE ELECTRODEPOSITION OF ZN-CO ALLOY FROM A ZINCATE BATH
    TU, ZM
    ZHANG, JS
    LI, WL
    YANG, ZL
    AN, MZ
    TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 1995, 73 : 48 - 49
  • [6] Effect of some plating parameters on the electrodeposition of Zn-Co alloys from aqueous citrate baths
    El Rehim, SSA
    Ibrahim, MAM
    El Wahaab, SMA
    Dankeria, MM
    TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 1999, 77 : 31 - 36
  • [7] Effect of some plating parameters on the electrodeposition of Zn-Co alloys from aqueous citrate baths
    Abd El Rehim, S.S.
    Ibrahim, M.A.M.
    Abd El Wahaab, S.M.
    Dankeria, M.M.
    Transactions of the Institute of Metal Finishing, 1999, 77 (01): : 31 - 36
  • [8] Electrochemical study on the inhibitory effect of the underpotential deposition of zinc on Zn-Co alloy electrodeposition
    Roventi, G
    Bellezze, T
    Fratesi, R
    ELECTROCHIMICA ACTA, 2006, 51 (13) : 2691 - 2697
  • [9] A combined composition. and morphology study of electrodeposited Zn-Co and Zn-Co-Fe alloy coatings
    Lodhi, Z. F.
    Tichelaar, F. D.
    Kwakemaak, C.
    Mol, J. M. C.
    Terryn, H.
    de Wit, J. H. W.
    SURFACE & COATINGS TECHNOLOGY, 2008, 202 (12): : 2755 - 2764
  • [10] Electrodeposition and characterization of thin layers of Zn-Co alloys obtained from glycinate baths
    Rashwan, SM
    Mohamed, AE
    Abdel-Wahaab, SM
    Kamel, MM
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 2003, 33 (11) : 1035 - 1042
12345