Study on stress relaxation characteristics of FGH95 powder superalloy treated by laser shock peening

Aiming at the phenomenon that the residual stress induced by Laser Shock Peening (LSP) will relax and redistribute under various loads, temperature, cyclic load, and the dual treatment of temperature and cyclic load on the residual stress relaxation of FGH95 powder superalloy after LSP treatment were studied, and the analysis model of relevant residual stress relaxation was constructed. The purpose is to understand the strengthening effect and stability of the alloy under temperature and cyclic load after LSP treatment. With the increase of treatment temperature, the relaxation of residual stress became more and more obvious. Most of the residual stress relaxation occurred in the first 30 min of temperature treatment, then slowed down and stabilized after 1 h. The residual stress was initially relaxed in the first 50 cycles, remained roughly unchanged between 50 and 5000 cycles. The intensify of the cyclic load increasing, adding material yield level, further plastic deformation and residual stress relaxation rate increases. With the increase of load intensify and load ratio, residual stress relaxation was also increased. The residual stress relaxation rate after 600 degrees C and cyclic load treatment was 56.2%, both greater than that after 600 degrees C or cyclic treatment of 25 degrees C, but less than the sum of the two conditions. The results of this paper provide a reference for the LSP of the FGH95 powder superalloy turbine disk and other aero engine parts.