An Investigation of the Polishing Behavior of Calcined Bauxite Aggregate

The application of top-grade calcined bauxite to improve the skid resistance of pavement surface coatings increases construction costs and causes excessive tire wear. Therefore, it is necessary to investigate the polishing behavior of different grades of calcined bauxite aggregate. The polished stone value of calcined bauxite was measured after the standard polishing time and the extended polishing time. The Los Angeles (L.A.) abrasion and the crushing value, profile roughness, hardness, X-ray diffraction, and micromorphology were also tested. The results showed that the calcined bauxite above 75# (the ratio of corundum to mullite by weight, C/M > 1) satisfied the requirement of the ultra-thin friction course. Compared with basalt, the calcined bauxite above 80# (C/M > 3) has better long-term skid resistance, even though the pavement surface is subject to heavier traffic. Due to the higher cohesion of lower porosity, more hard minerals to keep the surface roughness, and less soft minerals to smooth the surface roughness, calcined bauxite with a higher corundum content has the better skid resistance. There is a power law relationship between C/M and Polished Stone Value (PSV). Considering the diminishing returns of higher-grade calcined bauxite, it is necessary to accurately select the appropriate C/M of calcined bauxite before use in pavement surface coatings.