Low-Temperature Sintered K0.5Na0.5NbO3-Based Ceramics for Vibratory Gyro-sensor Applications

被引：2
|
作者：
Wong, Mau Tak [1 ]
Kwok, Kin Wing
机构：
[1] Hong Kong Polytech Univ, Dept Appl Phys, Kowloon, Hong Kong, Peoples R China
来源：
INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY | 2015年 / 12卷
关键词：
PIEZOELECTRIC PROPERTIES;
D O I：
10.1111/ijac.12344
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
0.91K(0.47)Na(0.47)Li(0.06)NbO(3)-0.09NaSbO(3) lead-free piezoelectric ceramics were prepared at 1000 degrees C using a sintering aid comprising of Cu and Ba in a molar ratio of 71.5/28.5. A dense structure with a high density of 4.43g/cm(3) was obtained for the ceramic added with 2.5 wt% of the sintering aid. Probably due to the smaller grains and doping of Cu2+, the piezoelectric coefficient and dielectric loss were reduced to 120 pC/N and 1.0%, respectively. The ceramics were then fabricated into vibratory gyro sensors of dimensions 0.6mmx0.6mmx4mm; and good sensitivity (0.7mV/dps) was obtained in the range of -360 to 360dps.
引用
收藏
页码：E149 / E155
页数：7
相关论文
共 50 条
  • [1] Low-temperature sintering of K0.5Na0.5NbO3 ceramics
    Bernard, Janez
    Bencan, Andreja
    Rojac, Tadej
    Holc, Janez
    Malic, Barbara
    Kosec, Marija
    Journal of the American Ceramic Society, 2008, 91 (07): : 2409 - 2411
  • [2] Low-temperature sintering of K0.5Na0.5NbO3 ceramics
    Bernard, Janez
    Bencan, Andreja
    Rojac, Tadej
    Holc, Janez
    Malic, Barbara
    Kosec, Marija
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2008, 91 (07) : 2409 - 2411
  • [3] K0.5Na0.5NbO3-Based Self-Powered Pressure Sensor
    Wang, Zhe
    Xue, Qingtang
    Yang, Yi
    Shu, Yi
    Tian, He
    Tang, Min
    Huan, Yu
    Wang, Xiaohui
    Luo, Janwen
    Ren, Tian-Ling
    TSINGHUA SCIENCE AND TECHNOLOGY, 2015, 20 (03) : 264 - 269
  • [4] K0.5Na0.5NbO3-Based Self-Powered Pressure Sensor
    Zhe Wang
    Qingtang Xue
    Yi Yang
    Yi Shu
    He Tian
    Min Tang
    Yu Huan
    Xiaohui Wang
    Janwen Luo
    Tian-Ling Ren
    TsinghuaScienceandTechnology, 2015, 20 (03) : 264 - 269
  • [5] Influence of zirconium addition on final properties of K0.5Na0.5NbO3-based ceramics
    Ramajo, L.
    Taub, J.
    Castro, M. S.
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2014, 25 (01) : 168 - 173
  • [6] Piezoelectric enhancements in K0.5Na0.5NbO3-based ceramics via structural evolutions
    Izzuddin, Izura
    Jumal, Mohammad Hafizuddin Hj
    Zainuddin, Zalita
    Janil, Nor Huwaida
    CERAMICS INTERNATIONAL, 2019, 45 (14) : 17204 - 17209
  • [7] Influence of zirconium addition on final properties of K0.5Na0.5NbO3-based ceramics
    L. Ramajo
    J. Taub
    M. S. Castro
    Journal of Materials Science: Materials in Electronics, 2014, 25 : 168 - 173
  • [8] Low-Temperature Sintering of (K0.5Na0.5)NbO3 Piezoelectric Ceramics
    Pang, Xuming
    Qiu, Jinhao
    Zhu, Kongjun
    Gu, Honghui
    JOURNAL OF INORGANIC AND ORGANOMETALLIC POLYMERS AND MATERIALS, 2013, 23 (02) : 463 - 466
  • [9] Low-Temperature Sintering of (K0.5Na0.5)NbO3 Piezoelectric Ceramics
    Xuming Pang
    Jinhao Qiu
    Kongjun Zhu
    Honghui Gu
    Journal of Inorganic and Organometallic Polymers and Materials, 2013, 23 : 463 - 466
  • [10] K0.5Na0.5NbO3-based multifunctional transparent ceramics for ultrahigh sensitive optical thermometry
    Liu, Hua
    Yang, Siqi
    Mo, Xiyang
    Guo, Mingsheng
    Tang, Haolin
    Zeng, Qingchao
    Ye, Mao
    Zheng, Renkui
    Ke, Shanming
    JOURNAL OF ADVANCED CERAMICS, 2025, 14 (03):
12345