Enhanced performance of dye-sensitized solar cells based on organic dopant incorporated PVDF-HFP/PEO polymer blend electrolyte with g-C3N4/TiO2 photoanode

This work describes the effect of 2-aminopyrimidine (2-APY) on poly(vinylidinefluoride-co-hexafluoropropylene) (PVDF-HFP)/polyethylene oxide (PEO) blend polymer electrolyte along with binary iodide salts (tetrabutylammonium iodide (TBAI) and potassium iodide (KI)) and iodine (I-2) were studied for enhancing the efficiency of the dye-sensitized solar cells (DSSCs) consisting of g-C3N4/TiO2 composite as photoanode. The g-C3N4 was synthesized from low cost urea by thermal condensation method. It was used as a precursor to synthesize the various weight percentage ratios (5%, 10% and 15%) of g-C3N4/TiO2 composites by wet -impregnation method. The pure and 2-APY incorporated PVDF-HFP/PEO polymer blend electrolytes were arranged by wet chemical process (casting method) using DMF as a solvent. The synthesized g-C3N4/TiO2 composites and polymer blend electrolytes were studied and analyzed by Fourier transform infrared (FT-IR) spectroscopy, X-ray diffractometer (XRD) and scanning electron microscopy (SEM). The ionic conductivity values of the pure and 2-APY incorporated PVDF-HFP/PEO blend electrolytes were estimated to be 4.53 x 10(-5) and 1.87 x 10(-4) Scm(-1) respectively. The UV-vis absorption spectroscopy was carried out for the pure and different wt% of g-C3N4/TiO2 composites coated FTO films after N3 dye-sensitization. The 10 wt% g-C3N4/TiO2 composite film showed a maximum absorption compared to the others. The DSSC assembled with 10 wt%g-C3N4/TiO2 as photoanode using the pure polymer blend electrolyte exhibited a power conversion efficiency (PCE) of 3.17%, which was superior than that of DSSC based pure TiO2 (2.46%). However, the PCE was increased to 4.73% for the DSSC assembled using 10 wt% g-C3N4/TiO2 as photoanode with 2-APY incorporated polymer blend electrolyte. Hence, the present study is a successful attempt to provide a new pathway to enhance the performance of DSSCs. (C) 2016 Elsevier Inc. All rights reserved.