Preparation of Pt/Al2O3 metallic honeycomb catalyst and its catalytic properties for CO preferential oxidation

被引：0

作者：

Zhang Jianguo ^{[1
,2
]}

Jia Jingsheng ^{[1
]}

Zhang Chunxi ^{[1
]}

Wang Shudong ^{[1
]}

机构：

[1] Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Peoples R China

[2] Chinese Acad Sci, Grad Univ, Beijing 10049, Peoples R China

来源：

CHINESE JOURNAL OF CATALYSIS | 2008年 / 29卷 / 05期

关键词：

metallic honeycomb catalyst; high-temperature oxidation; carbon monoxide; preferential oxidation;

D O I：

暂无

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

A Pt/Al2O3 metallic honeycomb catalyst was prepared and studied in the CO preferential oxidation. The surface of the Fe-20Cr-5Al metallic substrate (400 cells/in(2)) appeared needle shape structure when it was oxided at 900 degrees C for 10 h. The optimal Al2O3 coating procedure was slurry-sol-slurry. The metallic honeycomb catalyst showed CO conversion of 54.0% and CO selectivity of 42.5% in CO preferential oxidation at 120 C, which were 1.7 and 1.4 times that of the ceramic honeycomb catalyst, respectively.

引用

页码：421 / 425

页数：5

共 20 条

[1] Oxidation of FeCrAl alloy: influence of temperature and atmosphere on scale growth rate and mechanism
Badini, C
Laurella, F
[J]. SURFACE & COATINGS TECHNOLOGY, 2001, 135 (2-3): : 291 - 298
[2] CAO P, 2004, IND CATAL, V12, P41
[3] Carbon emission control strategies for China: A comparative study with partial and general equilibrium versions of the China MARKAL model
Chen, Wenying
Wu, Zongxin
He, Jiankun
Gao, Pengfei
Xu, Shaofeng
[J]. ENERGY, 2007, 32 (01) : 59 - 72
[4] CHEN ZZ, 2005, TECHNOL NEW PROCESS, V5, P62
[5] Effect of rare earth on the thermostability and the surface area of auto-catalyst washcoats
Ding, HM
Weng, D
Wu, XD
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2000, 311 (01) : 26 - 29
[6] Selective CO oxidation in H2-rich gas over K2CO3-promoted Rh/SiO2 catalysts:: effects of preparation method
Ito, S
Tanaka, H
Minemura, Y
Kameoka, S
Tomishige, K
Kunimori, K
[J]. APPLIED CATALYSIS A-GENERAL, 2004, 273 (1-2) : 295 - 302
[7] Li Q., 2001, SURF TECHNOL, V30, P23
[8] Liu CT, 2004, CHINESE J CATAL, V25, P697
[9] [刘煊 Liu Xuan], 2005, [贵金属, Precious Metals], V26, P12
[10] MATSUMOTO S, 1988, Patent No. 4742038

← 1 2 →