Composition dependence and irradiation effects on residual resistivity in Cu-Al alloys

Residual electrical resistivity due to short-range order has been calculated for Cu100-xAlx (x=9.13, 13.56, 14.5 and 14.76 in at pct) alloys using pseudopotential approach, and the results have been discussed in the light of experimental studies of the local-order structure of these alloys. In case of Cu85.5Al14.5, change in the total residual electrical resistivity due to neutron-irradiation effects has been estimated by including contributions from the short-range order and static atomic displacement correction. Our results show a decrease in the residual resistivity in the irradiated Cu-Al solid solution as compared to the unirradiated sample. This is in accordance with the experimental results.