Pre-oxidation Effect on Oxidation Behavior of F91 in Carbon Dioxide at 550°C

被引：9
|
作者：
Zheng, Yu [1 ]
Bidabadi, Mohammad Hassan Shirani [1 ]
Yang, Liang [1 ]
Rehman, Abdul [1 ]
Zhang, Chi [1 ]
Chen, Hao [1 ]
Yang, Zhi-Gang [1 ]
机构：
[1] Tsinghua Univ, Dept Mat Sci & Engn, Key Lab Adv Mat, Minist Educ, Beijing 100084, Peoples R China
来源：
OXIDATION OF METALS | 2018年 / 90卷 / 3-4期
关键词：
Pre-oxidation; Corrosion resistance; Carbon dioxide; 9Cr steel; FERRITIC FE-CR; SELECTIVE OXIDATION; BREAKAWAY OXIDATION; CHROMIA SCALES; ALLOYS; CARBURIZATION; CORROSION; MECHANISMS; STEELS; GASES;
D O I：
10.1007/s11085-018-9850-9
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Upon exposure to CO2 at 550 degrees C, F91 tends to form rapidly growing scales consisting of an outer Fe oxide and an inner Fe-Cr spinel oxide. A comparative study has been carried out between the pre-oxidized and non-pre-oxidized F91, to determine the influence of pre-oxidation upon the oxidation behavior of F91 in CO2. Formation of a rapidly growing scale and carburization could be inhibited by a pre-oxidation treatment in air prior to oxidation in CO2. Although during exposure to CO2, a fast growing scale still would form locally, pre-oxidation changed its structure. Effects of pre-oxidation time on the oxidation resistance in CO2 are investigated.
引用
收藏
页码：317 / 335
页数：19
相关论文
共 50 条
  • [1] Pre-oxidation Effect on Oxidation Behavior of F91 in Carbon Dioxide at 550 °C
    Yu Zheng
    Mohammad Hassan Shirani Bidabadi
    Liang Yang
    Abdul Rehman
    Chi Zhang
    Hao Chen
    Zhi-Gang Yang
    [J]. Oxidation of Metals, 2018, 90 : 317 - 335
  • [2] High-Temperature Oxidation Behavior of CrMoV, F91 and Mar-M247 Superalloys Exposed to Laboratory Air at 550°C
    Bidabadi, Mohammad Hassan Shirani
    Yu, Zheng
    Rehman, Abdul
    He, Jian Guo
    Zhang, Chi
    Chen, Hao
    Yang, Zhi-Gang
    [J]. OXIDATION OF METALS, 2018, 90 (3-4): : 401 - 419
  • [3] Ammonia modification of activated carbon to enhance carbon dioxide adsorption: Effect of pre-oxidation
    Shafeeyan, Mohammad Saleh
    Daud, Wan Mohd Ashri Wan
    Houshmand, Amirhossein
    Arami-Niya, Arash
    [J]. APPLIED SURFACE SCIENCE, 2011, 257 (09) : 3936 - 3942
  • [4] High-Temperature Oxidation Behavior of CrMoV, F91 and Mar-M247 Superalloys Exposed to Laboratory Air at 550 °C
    Mohammad Hassan Shirani Bidabadi
    Zheng Yu
    Abdul Rehman
    Jian Guo He
    Chi Zhang
    Hao Chen
    Zhi-Gang Yang
    [J]. Oxidation of Metals, 2018, 90 : 401 - 419
  • [5] Effect of pre-oxidation on cyclic oxidation resistance of γ-TiAl at 900 °C
    Swadzba, R.
    Laska, Nadine
    Bauer, Peter-Philipp
    Krzton, H.
    [J]. CORROSION SCIENCE, 2020, 177
  • [6] Beneficial effects of flame pre-oxidation on the oxidation behavior of NiCoCrAlHf alloy at 1050°C
    Yang, Bixiao
    Song, Peng
    Huang, Taihong
    Li, Chao
    Zhai, Ruixiong
    Ahmad, Syed Awais
    [J]. JOURNAL OF MATERIALS RESEARCH, 2022, 37 (09) : 1638 - 1650
  • [7] Effect of pre-oxidation at low temperature on the carbonization behavior of coal
    Worasuwannarak, N
    Nakagawa, H
    Miura, K
    [J]. FUEL, 2002, 81 (11-12) : 1477 - 1484
  • [8] Effect of pre-oxidation on NDMA precursors
    Selbes, Meric
    Kim, Daekyun
    Karanfil, Tanju
    [J]. ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2014, 248
  • [9] Effect of pre-oxidation on the oxidation resistance of Crofer 22 APU
    Talic, Belma
    Molin, Sebastian
    Hendriksen, Peter Vang
    Lein, Hilde Lea
    [J]. CORROSION SCIENCE, 2018, 138 : 189 - 199
  • [10] Effect of platinum and pre-oxidation on the hot corrosion behavior of aluminide coating with NaCl at 1050 °C
    Peng, Jubo
    Huang, Taihong
    Song, Peng
    Huang, Wenlang
    He, Yang
    Ma, Tao
    Yang, Bixiao
    Liang, Yuwei
    Wu, Minxuan
    Chen, Rong
    [J]. MATERIALS RESEARCH EXPRESS, 2020, 7 (11)
12345