Biocorrosion study of titanium-nickel alloys

The present study provides results of the corrosion behaviour In Hank's physiological solution and some other properties of three Ti-Ni alloys with 18, 25 and 28.4 wt% Ni, respectively. Results indicate that a-titanium and Ti,Ni were the two major phases in all three Ti-Ni alloys. The relative amount of the Ti,Ni phase increased with additional Ni content. Hardness of the Ti-Ni alloys also increased with added nickel content, ranging from 310 to 390 VHN, similar to the hardness of enamel. Melting temperatures of the Ti-Ni alloys were all lower than that of pure titanium by least 600 degrees C. The three Ti-Ni alloys behaved almost identically when potentiodynamically polarized in Hank's solution at 37 degrees C. The critical anodic current densities of the alloys were nearly 30 mu A/cm(2) and the breakdown potentials were all above 1100 mV (SCE).