Corrosion of Monel-400 in Aerated Stagnant Arabian Gulf Seawater after Different Exposure Intervals

被引：1

作者：

Sherif, El-Sayed M. ^{[1
,4
]}

Almajid, A. A. ^{[1
,2
]}

Bairamov, A. K. ^{[3
]}

Al-Zahrani, Eissa ^{[3
]}

机构：

[1] King Saud Univ, Coll Engn, CEREM, Riyadh 11421, Saudi Arabia

[2] King Saud Univ, Coll Engn, Dept Mech Engn, Riyadh 11421, Saudi Arabia

[3] SABIC Technol Ctr, SABIC, Mat & Corros Sect, Jubail Ind City 31961, Saudi Arabia

[4] Natl Res Ctr, Dept Phys Chem, Electrochem & Corros Lab, Cairo 12622, Egypt

来源：

INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE | 2011年 / 6卷 / 11期

关键词：

corrosion; Monel-400; alloy; EIS; polarization; SEM; weight loss; SODIUM-CHLORIDE SOLUTIONS; COPPER-NICKEL-ALLOYS; STAINLESS-STEEL; PITTING CORROSION; RESISTANT ALLOYS; DISK ELECTRODE; NACL SOLUTIONS; BEHAVIOR; INHIBITION; DISSOLUTION;

D O I：

暂无

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

The corrosion of Monel-400 after varied exposure periods in naturally aerated Arabian Gulf seawater (AGS) has been carried out using gravimetric, cyclic potentiodynamic polarization, chronoamperometry, open-circuit potential, and impedance spectroscopy measurements along with SEM/EDX investigations. Gravimetric data within 160 days showed that the weight loss increased, while the corrosion rate decreased with time. SEM/EDX investigations after 160 days immersion indicated that dissolution of Monel takes place due to the selective dissolution of Ni. The electrochemical measurements confirmed the gravimetric data and proved that severity of uniform corrosion of Monel decreases, while pitting one increases with increasing the exposure period.

引用

页码：5430 / 5444

页数：15

共 8 条

[1] A comparative Study on the Corrosion of Monel-400 in Aerated and Deaerated Arabian Gulf Water and 3.5% Sodium Chloride Solutions
Sherif, El-Sayed M.
Almajid, A. A.
Bairamov, A. K.
Al-Zahrani, Eissa
[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2012, 7 (04): : 2796 - 2810
[2] Effects of exposure time on the anodic dissolution of Monel-400 in aerated stagnant sodium chloride solutions
Sherif, El-Sayed M.
[J]. JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2012, 16 (03) : 891 - 899
[3] Effects of exposure time on the anodic dissolution of Monel-400 in aerated stagnant sodium chloride solutions
El-Sayed M. Sherif
[J]. Journal of Solid State Electrochemistry, 2012, 16 : 891 - 899
[4] Corrosion Behavior of Cast Iron in Freely Aerated Stagnant Arabian Gulf Seawater
Sherif, El-Sayed M.
Abdo, Hany S.
Almajid, Abdulhakim A.
[J]. MATERIALS, 2015, 8 (05) : 2127 - 2138
[5] Effect of different anions on pitting corrosion behaviour of Monel-400 in sea water
Gouda, VK
Khedr, AA
Fathi, AM
[J]. BULLETIN OF ELECTROCHEMISTRY, 2000, 16 (07): : 289 - 295
[6] Anodic Dissolution of API X70 Pipeline Steel in Arabian Gulf Seawater after Different Exposure Intervals
Sherif, El-Sayed M.
Almajid, Abdulhakim A.
[J]. JOURNAL OF CHEMISTRY, 2014, 2014
[7] Corrosion Inhibition of Cast Iron in Arabian Gulf Seawater by Two Different Ionic Liquids
Sherif, El-Sayed M.
Abdo, Hany S.
El Abedin, Sherif Zein
[J]. MATERIALS, 2015, 8 (07): : 3883 - 3895
[8] A Comparative Study on the Electrochemical Corrosion Behavior of Iron and X-65 Steel in 4.0 wt % Sodium Chloride Solution after Different Exposure Intervals
Sherif, El-Sayed M.
[J]. MOLECULES, 2014, 19 (07): : 9962 - 9974

← 1 →