Effect of machining-induced surface residual stress on initiation of stress corrosion cracking in 316 austenitic stainless steel

被引：120
|
作者：
Zhang, Wenqian [1 ]
Fang, Kewei [2 ]
Hu, Yujin [1 ]
Wang, Siyang [1 ]
Wang, Xuelin [1 ]
机构：
[1] Huazhong Univ Sci & Technol, Sch Mech Sci & Engn, State Key Lab Digital Mfg Equipment & Technol, Wuhan 430074, Peoples R China
[2] Suzhou Nucl Power Res Inst, Suzhou 215004, Peoples R China
来源：
CORROSION SCIENCE | 2016年 / 108卷
基金：
中国国家自然科学基金;
关键词：
Stainless steel; Stress corrosion; CHLORIDE SOLUTION; HIGH-TEMPERATURE; PIPELINE STEELS; PART; BEHAVIOR; RESISTANCE; WATER; MICROSTRUCTURE; SUSCEPTIBILITY; PROPAGATION;
D O I：
10.1016/j.corsci.2016.03.008
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of machining-induced surface residual stress on the stress corrosion cracking (SCC) initiation in 316 stainless steel was investigated in boiling magnesium chloride solution. The crack density was used to evaluate the SCC initiation and propagation at different residual stress levels. The results showed a strong correlation between the residual stress and the resultant micro-crack density. When the residual stress reached a critical value, the micro-crack density increased significantly in the very early phase, and the critical stress is 190 MPa for 316 stainless steel. Additionally, the cracking behavior could be correlated with the machining effects on the surface layer. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：173 / 184
页数：12
相关论文
共 50 条
  • [1] Comprehensive Impact of Machined Surface Integrity on Stress Corrosion Cracking Initiation in 316 Austenitic Stainless Steel
    Liu, Zongyi
    Zhang, Wenqian
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025, 34 (05) : 4230 - 4239
  • [2] Effect of machining-induced surface topography on corrosion behaviors of 304 austenitic stainless steel in pre-stress grinding
    Zhuangzhuang Hou
    Shichao Xiu
    Cong Sun
    Yunlong Yao
    The International Journal of Advanced Manufacturing Technology, 2022, 122 : 2971 - 2985
  • [3] Effect of machining-induced surface topography on corrosion behaviors of 304 austenitic stainless steel in pre-stress grinding
    Hou, Zhuangzhuang
    Xiu, Shichao
    Sun, Cong
    Yao, Yunlong
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2022, 122 (7-8): : 2971 - 2985
  • [4] STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEEL
    MAREK, M
    HOCHMAN, RF
    CORROSION, 1970, 26 (01) : 5 - &
  • [5] Film-stress induced stress corrosion cracking of austenitic stainless steel
    Li, JX
    Wang, YB
    Qiao, LJ
    Chu, WY
    ACTA METALLURGICA SINICA, 2002, 38 (08) : 861 - 865
  • [6] Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
    Rahimi, S.
    Mehrez, K.
    Marrow, T. J.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2016, 51 (05) : 383 - 391
  • [7] Film-stress induced stress corrosion cracking of austenitic stainless steel
    Li, Jinxu
    Wang, Yanbin
    Qiao, Lijie
    Chu, Wuyang
    Jinshu Xuebao/Acta Metallurgica Sinica, 2002, 38 (08):
  • [8] Effect of residual stress induced by pulsed-laser irradiation on initiation of chloride stress corrosion cracking in stainless steel
    Eto, Shuzo
    Miura, Yasufumi
    Tani, Junichi
    Fujii, Takashi
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 590 : 433 - 439
  • [9] Stress corrosion cracking initiation in austenitic stainless steel in high temperature water
    Matocha, K
    Wozniak, J
    PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 383 - 388
  • [10] Modelling Hydrogen Induced Stress Corrosion Cracking in Austenitic Stainless Steel
    Ogosi, E., I
    Asim, U. B.
    Siddiq, M. A.
    Kartal, M. E.
    JOURNAL OF MECHANICS, 2020, 36 (02) : 213 - 222
12345