Study on lightly sulfonated syndiotactic polystyrene ionomers

Sulfonated syndiotactic polystyrene ionomers (SsPS) with 1.8 mol% degree of sulfonation have been studied. WAXD shows that the crystallinity of SsPS ionomers was decreased with increasing diameter size of the counter ions and sPS > SsPS-H > SsPS-K > SsPS-Zn. Moreover, SsPS ionomers only have alpha crystal form, while original sPS has two crystal forms: alpha and beta crystal form. TGA shows that the thermal stability of SsPS ionomers is higher than that of the original sPS and SsPS-Zn > SsPS-K > SsPS-H. DSC shows that all the glass transition temperatures (T-g) of SsPS ionomers are higher than that of the neat sPS and SsPS-Zn > SsPS-Na > SsPS-K > SsPS-H. However, the melting temperature (T-m) and crystallization peak temperature (T-p) of SsPS ionomers are lower and SsPS-H > SsPS-Zn > SsPS-K > SsPS-Na, while the crystallinity (X-c) of SsPS-Zn is the lowest. Nonisothermal crystallization kinetics shows that the Avrami index of sPS and SsPS-H are both about 4, suggesting the nucleation growth of SsPS-H with lower degree of sulfonation still keeps its three-dimension form. FTIR spectra of SsPS ionomers show a splitting absorption band for asymmetric stretching vibration of sulfonation group. The CH in-plane bending vibration of benzene ring shifted to higher wavenumber and the symmetric stretching vibration of sulfonation group changed slightly with different counter ion neutralized SsPS ionomers.