Investigation of caustic stress corrosion cracking of a carbon steel by slow strain rate testing

被引：3
|
作者：
Raman, RKS [1 ]
Muddle, BC [1 ]
机构：
[1] Monash Univ, Sch Phys & Mat Engn, Clayton, Vic 3168, Australia
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2003年 / 19卷 / 05期
关键词：
D O I：
10.1179/026708303225010812
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This paper presents results of an experimental investigation of stress corrosion cracking (SCC) of a carbon steel in a typical synthetic Bayer liquor (SBL), employing a slow strain rate testing (SSRT) technique. Fractographic details of SCC crack propagation of specimens tested in SBL and an inert environment have been compared.
引用
收藏
页码：642 / 644
页数：3
相关论文
共 50 条
  • [1] STRESS-CORROSION CRACKING OF CARBON-STEEL IN CAUSTIC ALUMINATE SOLUTIONS - SLOW STRAIN RATE STUDIES
    SRIRAM, R
    TROMANS, D
    [J]. CORROSION, 1985, 41 (07) : 381 - 385
  • [2] Some developments in slow strain rate testing for stress corrosion cracking
    Poulson, Bryan
    [J]. CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2012, 47 (03) : 209 - 222
  • [3] LIMITATIONS OF THE SLOW STRAIN RATE TEST FOR STRESS-CORROSION CRACKING TESTING
    BEAVERS, JA
    KOCH, GH
    [J]. CORROSION, 1992, 48 (03) : 256 - 264
  • [4] Stress Corrosion Cracking Behavior of Duplex Stainless Steel by Slow Strain Rate Tests
    Sanchez, J.
    Fullea, J.
    Andrade, C.
    Alonso, C.
    [J]. CORROSION, 2009, 65 (02) : 154 - 159
  • [5] Stress Corrosion Cracking Behavior of Interstitial Free Steel Via Slow Strain Rate Technique
    Pratik Murkute
    J. Ramkumar
    K. Mondal
    [J]. Journal of Materials Engineering and Performance, 2016, 25 : 2878 - 2888
  • [6] Stress Corrosion Cracking Behavior of Interstitial Free Steel Via Slow Strain Rate Technique
    Murkute, Pratik
    Ramkumar, J.
    Mondal, K.
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (07) : 2878 - 2888
  • [7] Stress corrosion cracking susceptibility of nickel-molybdenum alloys by slow strain rate and immersion testing
    Nakahara, M
    Shoji, T
    [J]. CORROSION, 1996, 52 (08) : 634 - 642
  • [8] Slow strain rate tensile testing for evaluating stress corrosion cracking of Type-40Cr steel in the acidic chloride solution
    Li-Juan, An
    Yong-Tao, Zhao
    Qing-Fen, Li
    [J]. ADVANCES IN FRACTURE AND DAMAGE MECHANICS VI, 2007, 348-349 : 877 - +
  • [9] Peridynamic investigation of stress corrosion cracking in carbon steel pipes
    Shi, Chunxiang
    Gong, Yi
    Yang, Zhen-Guo
    Tong, Qi
    [J]. ENGINEERING FRACTURE MECHANICS, 2019, 219
  • [10] CAUSTIC STRESS-CORROSION CRACKING OF MILD-STEEL
    SINGBEIL, D
    TROMANS, D
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (06): : 1091 - 1098
12345