The Effect of Tempering Temperature on Pitting Corrosion Resistance of 420 Stainless Steels

The AISI Type 420 stainless steels arc commonly used to steam generators, mixer blades, etc. These stainless steels are most prone to pitting in dissolved CF containing environments. In this paper, the effect of tempering temperature on pitting corrosion resistance of AISI Type 420 stainless steels was studied. The AISI Type 420 stainless steels specimens were heat treated at the temperature of 1050 degrees C for 1 hour to reach austenite stabilization and then quench in the oil. After that, the specimens were tempered at the temperature of 150, 250, 350 and 450 degrees C for 30 minutes and then air cooled to the room temperature. The electrochemical potentiodynamic polarization test was conducted at 3.5% sodium chloride solution to evaluate corrosion rate and pitting corrosion behaviour. The Scanning Electron Microscope (SEM), Energy Dispersive X-Ray Spectroscopy (EDS) were used to evaluate the pitting corrosion product. The result have shown that highest pitting potential was found in the sample tempered at 250 degrees C and corrosion pits were found to initiate preferentially around chromium carbides.