Effect of He-injection on irradiation damage of high Mn-Cr steel

被引：1
|
作者：
Bae, DS [1 ]
Lee, SP
Nahm, SH
Choi, JW
Takahashi, H
机构：
[1] Dong Eui Univ, Dept Mat & Met Engn, Pusan 614714, South Korea
[2] Dong Eui Univ, Dept Mech Engn, Pusan 614714, South Korea
[3] Korea Res Inst Stand & Sci, Ctr Environm & Safety Management, Taejon 305600, South Korea
[4] Def Qual Assurance Agcy, Changwon Div Branch 2, Chang Won 641600, South Korea
[5] Hokkaido Univ, Ctr Adv Res Energy Technol, Sapporo, Hokkaido 0608628, Japan
来源：
PRICM 5: THE FIFTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-5 | 2005年 / 475-479卷
关键词：
irradiation damage; electron-beam irradiation; electron/He+-ion dual-beam irradiation; electron-beam irradiation after He-injection; high Mn-Cr steel; high voltage electron microscope; in-situ observation; void; irradiation-induced segregation;
D O I：
10.4028/www.scientific.net/MSF.475-479.1425
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The high Mn-Cr austenitic steel for structure material of nuclear and/or fusion reactors from the point of view of the reduced radio-activation has been irradiated by using three irradiation modes of electron-beam irradiation, electron-beam irradiation after He-injection and electron/He+-ion dual-beam irradiation in 1250kV high voltage electron microscope (HVEM) connected with an ion accelerators to study the effect of He-injection on irradiation damage. Irradiation-induced segregation analyses were carried out by an energy dispersive X-ray analyzer (EDX) in a 200kV FE-TEM with beam diameter of about 0.5nm. Void formation was not observed in each irradiation condition. Grain boundary migration was observed in the case of electron/He+-ion dual-beam irradiation. Irradiation-induced segregations of Cr and Mn at grain boundary were observed in each irradiation condition. The amounts of Cr and Mn segregation decreased in the cases of electron-beam irradiation after He-injection compared with other irradiation conditions.
引用
收藏
页码：1425 / 1428
页数：4
相关论文
共 50 条
  • [1] Effect of He-injection on irradiation-induced segregation of aging treated high Mn-Cr steel
    Bae, Dong-Su
    Jeong, Ho-Shin
    JOURNAL OF THE KOREAN INSTITUTE OF METALS AND MATERIALS, 2007, 45 (07): : 397 - 402
  • [2] Effect of electron-beam irradiation temperature on irradiation damage of high Mn-Cr steel
    Bae, DS
    Nahm, SH
    Lee, HM
    Kinoshita, H
    Shibayama, T
    Takahashi, H
    JOURNAL OF NUCLEAR MATERIALS, 2004, 329 : 1038 - 1042
  • [3] Effect of He-injection on irradiation damage in heat affected zone of welded SUS304 steel
    Bae, DS
    Kinoshita, H
    Shibayama, T
    Takahashi, H
    MATERIALS TRANSACTIONS, 2004, 45 (01) : 59 - 64
  • [4] Effect of aging treatment on irradiation-induced segregation of high Mn-Cr steel
    D.S.BAE
    S.P.LEE
    Y.R.CHO
    H.TAKAHASHI
    TransactionsofNonferrousMetalsSocietyofChina, 2011, 21(S1) (S1) : 58 - 61
  • [5] Effect of aging treatment on irradiation-induced segregation of high Mn-Cr steel
    Bae, D. S.
    Lee, S. P.
    Cho, Y. R.
    Takahashi, H.
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2011, 21 : S58 - S61
  • [6] Evaluation of creep damage in a Mn-Cr austenitic steel
    Matera, R., 1600, (23):
  • [7] EVALUATION OF CREEP DAMAGE IN A MN-CR AUSTENITIC STEEL
    MATERA, R
    SCRIPTA METALLURGICA, 1989, 23 (01): : 65 - 70
  • [8] The effect of microstructure on the localised corrosion behavior of a high strength Mn-Cr austenitic steel
    Mukhopadhyay, N
    Chatterjee, UK
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1997, 50 (01): : 49 - 58
  • [9] Dynamic Recrystallization Behavior in Mn-Cr Gear Steel
    WANG Bing-xin 1
    2. State Key Laboratory of Rolling and Automation
    Journal of Iron and Steel Research(International), 2006, (02) : 49 - 53
  • [10] Dynamic recrystallization behavior in Mn-Cr gear steel
    Wang, BX
    Xu, XD
    Liu, XH
    Wang, GD
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2006, 13 (02) : 49 - 53
12345