Formation of Alumina Layer on Fe-Cr-Ni Alloy by Pack Cementation and Oxidation

被引：2
|
作者：
Xing, Linlin [1 ]
Zheng, Yanjun [1 ]
Cui, Lishan [1 ]
Sun, Maohu [1 ]
Shao, Mingzeng [1 ]
Lu, Guiwu [1 ]
机构：
[1] China Univ Petr, Dept Mat Sci & Engn, Beijing 102249, Peoples R China
来源：
HIGH TEMPERATURE MATERIALS AND PROCESSES | 2011年 / 30卷 / 1-2期
关键词：
High temperature alloy; coke deposition; oxidation; pack cementation; HIGH-TEMPERATURE OXIDATION; EARLY-STAGE; BEHAVIOR; VAPOR; CARBURIZATION; COATINGS; NI3AL;
D O I：
10.1515/HTMP.2011.013
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
To protect Fe-Cr-Ni based alloy from high temperature corrosion in carbon containing atmosphere at elevated temperature, alumina coating was prepared on the Fe-Ni-Cr alloy substrate by pack cementation and oxidation. Results showed that a surface FeAl layer formed after the pack cementation process, and an Al2O3 coating formed by selective oxidation of the FeAl layer. The coating adhered tightly to the FeAl layer without any cracks or porous inbetween them. By the oxidation process the catalytic elements such as Fe and Ni were remarkably reduced from the surface. Further anti-coking test indicated that the alumina scale could successfully inhibit the outward diffusion of catalytic elements and showed excellent coking resistance.
引用
收藏
页码：99 / 103
页数：5
相关论文
共 50 条
  • [1] Low temperature aluminising of Fe-Cr-Ni super alloy by pack cementation
    Yener, Tuba
    VACUUM, 2019, 162 : 114 - 120
  • [2] EFFECT OF A PLATED FE-CR-NI ALLOY LAYER FOR RAPID NITRIDING OF INVAR
    GEMMA, K
    KAWAKAMI, M
    UEDA, H
    MIHARA, C
    JOURNAL OF MATERIALS SCIENCE, 1992, 27 (13) : 3461 - 3466
  • [3] Formation of a blocky ferrite in Fe-Cr-Ni alloy during directional solidification
    Fu, J. W.
    Yang, Y. S.
    Guo, J. J.
    JOURNAL OF CRYSTAL GROWTH, 2009, 311 (14) : 3661 - 3666
  • [4] The Effect of Alloy Solidification Path on Sulfide Formation in Fe-Cr-Ni Alloys
    Nakama, Kazuo
    Haruna, Yasushi
    Nakano, Jinichiro
    Sridhar, Seetharaman
    ISIJ INTERNATIONAL, 2009, 49 (03) : 355 - 364
  • [5] Oxidation resistance of Fe-Cr-Ni laser cladding layer under supercritical water
    Cheng, Yan-Hai
    Ren, Lu
    Yi, Guo-Ming
    Wang, Shuai
    Li, Shi-Bin
    Liu, Cheng-Ze
    Wang, Qing-Guo
    Qin, Qiang
    SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES, 2020, 8 (02):
  • [6] Preparation and Oxidation Performance of Y and Ce-Modified Cr Coating on open-cell Ni-Cr-Fe Alloy Foam by the Pack Cementation
    Pang, Q.
    Hu, Z. L.
    Wu, G. H.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (12) : 5189 - 5200
  • [7] Preparation and Oxidation Performance of Y and Ce-Modified Cr Coating on open-cell Ni-Cr-Fe Alloy Foam by the Pack Cementation
    Q. Pang
    Z. L. Hu
    G. H. Wu
    Journal of Materials Engineering and Performance, 2016, 25 : 5189 - 5200
  • [8] Thermal stability of ultrafine grained Fe-Cr-Ni alloy
    Sun, C.
    Yang, Y.
    Liu, Y.
    Hartwig, K. T.
    Wang, H.
    Maloy, S. A.
    Allen, T. R.
    Zhang, X.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 542 : 64 - 70
  • [9] Dynamic compression of an Fe-Cr-Ni alloy to 80 GPa
    Duffy, TS
    Ahrens, TJ
    JOURNAL OF APPLIED PHYSICS, 1997, 82 (09) : 4259 - 4269
  • [10] Eutectic growth of unidirectionally solidified Fe-Cr-Ni alloy
    Okane, T
    Umeda, T
    ISIJ INTERNATIONAL, 1998, 38 (05) : 454 - 460
12345