Ion beam assisted deposited tantalum oxide coatings on aluminum

被引：39
|
作者：
Natishan, PM [1 ]
McCafferty, E [1 ]
Puckett, PR [1 ]
Michel, S [1 ]
机构：
[1] COMMONWEALTH SCI CORP,ALEXANDRIA,VA 22314
来源：
CORROSION SCIENCE | 1996年 / 38卷 / 07期
关键词：
aluminum; tantalum oxide; XPS; oxide coatings;
D O I：
10.1016/0010-938X(96)00185-0
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Ion beam assisted deposition (IBAD) and sputter deposition were used to produce tantalum oxide surfaces on aluminum substrate. The corrosion behavior of the sputter deposited coatings and IBAD modified regions was studied by anodic polarization in deaerated, 0.1M NaCl solutions. The electrochemical results showed that the tantalum oxide surfaces significantly improved the pitting corrosion resistance of the substrate metal. The best results were obtained for samples with 1.8 mu m thick tantalum oxide IBAD modified surfaces. These samples have an average pitting potential value that is 0.850 V higher than that of pure aluminum. X-ray photo-electron spectroscopy showed that the surface of the IBAD samples was composed of Ta2O5 as well as tantalum carbide and tantalum suboxide species. Published by Elsevier Science Ltd.
引用
收藏
页码：1043 / 1049
页数：7
相关论文
共 50 条
  • [1] Corrosion properties of alumina coatings on steel and aluminum deposited by ion beam assisted deposition
    Stippich, F
    Vera, E
    Scheerer, H
    Wolf, GK
    Jian-Ming, X
    SURFACE & COATINGS TECHNOLOGY, 1998, 98 (1-3): : 997 - 1001
  • [2] THE PITTING BEHAVIOR OF SILICON-NITRIDE ION-BEAM ASSISTED DEPOSITED COATINGS ON ALUMINUM
    NATISHAN, PM
    MCCAFFERTY, E
    DONOVAN, EP
    BROWN, DW
    HUBLER, GK
    SURFACE & COATINGS TECHNOLOGY, 1992, 51 (1-3): : 30 - 34
  • [3] MICROSTRUCTURAL VARIATIONS IN ALUMINUM-OXIDE COATINGS DEPOSITED USING A DUAL BEAM ION SYSTEM
    PANITZ, JKG
    HILLS, CR
    TALLANT, DR
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1990, 8 (03): : 1313 - 1317
  • [4] Microanalysis of tantalum oxide films deposited by dynamic ion beam mixing
    Du, Ji-Fu
    Zhan, Chang-Yong
    Huang, Ning-Kang
    Gongneng Cailiao yu Qijian Xuebao/Journal of Functional Materials and Devices, 2007, 13 (06): : 512 - 516
  • [5] Enhanced corrosion protection of magnesium oxide coatings on magnesium deposited by ion beam-assisted evaporation
    Stippich, F
    Vera, E
    Wolf, GK
    Berg, G
    Friedrich, C
    SURFACE & COATINGS TECHNOLOGY, 1998, 104 : 29 - 35
  • [6] OPTICAL-PROPERTIES OF TANTALUM PENTOXIDE COATINGS DEPOSITED USING ION-BEAM PROCESSES
    ALJUMAILY, GA
    EDLOU, SM
    THIN SOLID FILMS, 1992, 209 (02) : 223 - 229
  • [7] Preparation of aluminum oxide films by ion beam assisted deposition
    Shimizu, I
    Setsuhara, Y
    Miyake, S
    Kumagai, M
    Ogata, K
    Kohata, M
    Yamaguchi, K
    SURFACE & COATINGS TECHNOLOGY, 2000, 131 (1-3): : 187 - 191
  • [8] PROPERTIES OF THIN-FILMS OF TANTALUM OXIDE DEPOSITED BY ION-ASSISTED DEPOSITION
    MARTIN, PJ
    BENDAVID, A
    SWAIN, M
    NETTERFIELD, RP
    KINDER, TJ
    SAINTY, WG
    DRAGE, D
    WIELUNSKI, L
    THIN SOLID FILMS, 1994, 239 (02) : 181 - 185
  • [9] Optical properties of oxide coatings deposited by dual-ion-beam sputter
    Tang, Xuefei
    Fan, Zhengxiu
    Wang, Zhijiang
    Vacuum, 1991, 42 (16)
  • [10] CORROSION AND WEAR PROPERTIES OF MULTIPURPOSE COATINGS DEPOSITED BY ION-BEAM-ASSISTED DEPOSITION
    ENDERS, B
    MARTIN, H
    WOLF, GK
    SURFACE & COATINGS TECHNOLOGY, 1993, 60 (1-3): : 556 - 560
12345