Nano Serpentine Powders as Lubricant Additive: Tribological Behaviors and Self-Repairing Performance on Worn Surface

被引:39
|
作者
Wang, Binbin [1 ]
Zhong, Zhaodong [1 ]
Qiu, Han [1 ]
Chen, Dexin [1 ]
Li, Wei [1 ]
Li, Shuangjian [1 ]
Tu, Xiaohui [1 ]
机构
[1] Jinan Univ, Inst Adv Wear & Corros Resistance & Funct Mat, Guangzhou 510000, Peoples R China
基金
国家重点研发计划;
关键词
serpentine; lubricant additive; friction and wear; self-repairing; NATURAL SERPENTINE; MINERAL POWDERS; MICROSTRUCTURE;
D O I
10.3390/nano10050922
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
Natural serpentine powders are applicable as additives for various lubricating oils. However, no uniform theories explain their tribological performance, lubrication, and wear mechanism, especially their self-repairing mechanism. Herein, the influence of different nano serpentine powders (NSPs) contents in liquid paraffin on the friction and wear characteristics of steel balls and the self-repairing process of NSPs on the worn surface were studied. Results show that the optimal amount of NSPs was 0.5 wt %. Relative to those of the base oil, the friction coefficients and wear spot diameters were reduced by 22.8% and 34.2%, respectively. Moreover, the long-term tribological test shows that the wear scar diameter decreased slightly after 3 h, reaching the state of dynamic balance between wear and repair. The outstanding tribological performance should be attributed to the formed bilayer tribofilm, the first layer of which contains nanoparticles surrounded by lubricants and the second layer of which contains nanoparticles compacted onto the surface of the steel ball.
引用
收藏
页数:12
相关论文
共 46 条
  • [1] Research on Tribological Characteristics and Worn Surface Self-Repairing Performance of Nano Attapulgite Powders Used in Lubricant Oil as Addictive
    Zhang Bo
    Xu Binshi
    Xu Yi
    Gao Fei
    Zhang Baosen
    [J]. RARE METAL MATERIALS AND ENGINEERING, 2012, 41 : 336 - 340
  • [3] Tribological behaviors of surface-coated serpentine ultrafine powders as lubricant additive
    Yu, H. L.
    Xu, Y.
    Shi, P. J.
    Wang, H. M.
    Zhao, Y.
    Xu, B. S.
    Bai, Z. M.
    [J]. TRIBOLOGY INTERNATIONAL, 2010, 43 (03) : 667 - 675
  • [4] Self-repairing performance and formation mechanism of self-repairing layer of natural serpentine powder as a lubricating oil additive
    Gao, Fei
    Xu, Yi
    Xu, Bin-Shi
    Zhang, Bao-Sen
    Zhang, Bo
    Shi, Pei-Jing
    [J]. Mocaxue Xuebao/Tribology, 2011, 31 (05): : 431 - 438
  • [5] Self-repairing rule of lubricant with nano-zinc as an additive under point contact
    Yang, Chang-Jiang
    Chen, Guo-Xu
    Su, Bin
    Hua, Yan
    Liao, Zi-Jun
    [J]. Mocaxue Xuebao/Tribology, 2010, 30 (04): : 350 - 355
  • [6] Lanthanum Effect on the Tribological Behaviors of Natural Serpentine as Lubricant Additive
    Zhang, Bao-Sen
    Xu, Bin-Shi
    Xu, Yi
    Ba, Zhi-Xin
    Wang, Zhang-Zhong
    [J]. TRIBOLOGY TRANSACTIONS, 2013, 56 (03) : 417 - 427
  • [7] Technology of self-repairing and reinforcement of metal worn surface
    Yi Xu
    Fei Gao
    Bo Zhang
    Feng Nan
    Bin-Shi Xu
    [J]. Advances in Manufacturing, 2013, 1 (01) : 102 - 105
  • [8] Tribological Performance Research of Micro-nano Serpentine Powders Addictive to Lubricant Oil
    Zhang, Bo
    Xu, Yi
    Zhang, Baosen
    Xu, Binshi
    [J]. MATERIALS PROCESSING TECHNOLOGIES, PTS 1 AND 2, 2011, 154-155 : 220 - 225
  • [9] Technology of self-repairing and reinforcement of metal worn surface
    Xu, Yi
    Gao, Fei
    Zhang, Bo
    Nan, Feng
    Xu, Bin-Shi
    [J]. ADVANCES IN MANUFACTURING, 2013, 1 (01) : 102 - 105
  • [10] Technology of self-repairing and reinforcement of metal worn surface
    Yi Xu
    Fei Gao
    Bo Zhang
    Feng Nan
    Bin-Shi Xu
    [J]. Advances in Manufacturing, 2013, 1 : 102 - 105