Evaluation of metallic interconnects for use in intermediate temperature SOFC

被引：0
|
作者：
Armstrong, TJ [1 ]
Homel, MA [1 ]
Virkar, AV [1 ]
机构：
[1] Mat & Syst Res Inc, Salt Lake City, UT 84104 USA
来源：
SOLID OXIDE FUEL CELLS VIII (SOFC VIII) | 2003年 / 2003卷 / 07期
关键词：
D O I：
暂无
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Foil samples of Haynes 230 and 430 stainless steel were coated with thin layers of Mn and La metal, oxidized in air and humidified hydrogen atmospheres at 800degreesC for various periods of time, and evaluated for use as metallic interconnects in planar SOFC. A Mn-coating on the interconnects promoted the formation of the spinel phase (Mn, Cr)(3)O-4 while suppressing the formation of Cr2O3 during oxidation. The area specific resistance (ASR) of the oxide layer on the Mn-coated Haynes 230 samples (similar to0.24 Omegacm(2) at 800degreesC) was significantly less than that formed on the uncoated sample (similar to1.2 Omegacm(2) at 800degreesC). The oxide layer formed on the La-coated Haynes 230 consisted primarily of the perovskite phase La(Cr, Mn)O-3. The ASR of the perovskite oxide layer formed on the La-coated Haynes 230 was an order of magnitude lower than the oxide layer, primarily Cr2O3, formed on uncoated Haynes 230. Planar SOFC stacks operated with coated interconnects delivered double the maximum power and exhibited half the total stack resistance as compared to stacks operated with uncoated Haynes 230 interconnects.
引用
收藏
页码：841 / 850
页数：10
相关论文
共 50 条
  • [1] Ceramic coatings for metallic SOFC interconnects
    Fergus, Jeffrey W.
    [J]. TMS 2008 ANNUAL MEETING SUPPLEMENTAL PROCEEDINGS, VOL 1: MATERIALS PROCESSING AND PROPERTIES, 2008, : 555 - 560
  • [2] PROTECTIVE COATINGS FOR SOFC METALLIC INTERCONNECTS
    King, Mark K., Jr.
    Mahapatra, Manoj K.
    [J]. PROCEEDINGS OF THE 42ND INTERNATIONAL CONFERENCE ON ADVANCED CERAMICS AND COMPOSITES: CERAMIC ENGINEERING AND SCIENCE PROCEEDINGS, VOL 39, ISSUE 2, 2019, : 149 - 158
  • [3] Metallic interconnects for SOFC: Characterisation of corrosion resistance and conductivity evaluation at operating temperature of differently coated alloys
    Fontana, S.
    Amendola, R.
    Chevalier, S.
    Piccardo, P.
    Caboche, G.
    Viviani, M.
    Molins, R.
    Sennour, M.
    [J]. JOURNAL OF POWER SOURCES, 2007, 171 (02) : 652 - 662
  • [4] Advances in the development of metallic interconnects of SOFC cells
    Alvarado-Flores, J.
    [J]. BOLETIN DE LA SOCIEDAD ESPANOLA DE CERAMICA Y VIDRIO, 2013, 52 (04): : 194 - 206
  • [5] COATING OF SOFC METALLIC INTERCONNECTS AND THEIR OXYGEN DIFFUSIVITY
    Horita, Teruhisa
    [J]. PROCEEDINGS OF THE ASME 8TH INTERNATIONAL CONFERENCE ON FUEL CELL SCIENCE, ENGINEERING, AND TECHNOLOGY 2010, VOL 2, 2010, : 405 - 409
  • [6] Corrosion of metallic interconnects for SOFC in fuel gases
    Zeng, Z
    Natesan, K
    [J]. SOLID STATE IONICS, 2004, 167 (1-2) : 9 - 16
  • [7] Protective coatings of metallic interconnects for IT-SOFC application
    Bertoldi, M.
    Zandonella, T.
    Montinaro, D.
    Sglavo, V. M.
    Fossati, Alessio
    Lavacchi, A.
    Giolli, C.
    Bardi, U.
    [J]. JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY, 2008, 5 (01):
  • [8] Perovskite and Spinel Functional Coatings for SOFC Metallic Interconnects
    Brylewski, Tomasz
    Przybylski, Kazimierz
    [J]. HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 7, PTS 1 AND 2, 2008, 595-598 : 813 - 822
  • [9] Oxidation behavior of metallic interconnects for SOFC in coal syngas
    Li, Yihong
    Wu, Junwei
    Johnson, Christopher
    Gemmen, Randall
    Scott, X. Mao
    Liu, Xingbo
    [J]. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2009, 34 (03) : 1489 - 1496
  • [10] Evaluation of feritic steel interconnects for SOFC stacks
    Honegger, K
    Plas, A
    Diethelm, R
    Glatz, W
    [J]. SOLID OXIDE FUEL CELLS VII (SOFC VII), 2001, 2001 (16): : 803 - 810
12345