Preparation of Ultrafine AgO Powder and Silver Valence Change

被引：0

作者：

Shen Wenning ^{[1
]}

Feng Lajun ^{[1
]}

Kong Zhenzhen ^{[1
]}

机构：

[1] Xian Univ Technol, Dept Mat Phys & Chem, Xian 710048, Peoples R China

来源：

RARE METAL MATERIALS AND ENGINEERING | 2011年 / 40卷 / 11期

关键词：

silver peroxide; ozone; oxidation precipitation method; silver valence; XPS;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

High pure ultrafine AgO powder was synthesized by ozone oxidation of AgNO3. Silver valence change of AgO at different temperatures was determined by differential thermal analysis. AgO powder were also characterized by XRD, SEM and XPS to analyze the phase and morphology and the silver valence change of the powder heated at different temperatures. The results show that the crystal structure of the prepared ultrafine AgO powder belongs to monoclinic system and AgO particles are of virgulate shapes. The colour of ultrafine AgO powder changes obviously after heating. In the heating process, with increasing of the temperature, the content of AgO decreases gradually, the content of Ag2O increases firstly and then decreases and the content of Ag increases gradually. When the temperature exceeds 350 degrees C, AgO decompose completely, 46.49 % of which transforms into Ag2O and 53.51% transforms into Ag. And complete decomposition to Ag occurs at 400 degrees C. The XPS spectra of Ols on different powder surfaces are quite distinct, reflecting the lattice structure change of powder.

引用

页码：1961 / 1965

页数：5

共 11 条

[1] Antelman M.S., 1992, US Patent No. 5098582, Patent No. 5098582
[2] Huang Hansheng, 1996, DET COS, P7
[3] Ma Ruzhang, 1997, MODERN RES METHODS M, P206
[4] Meng Fanming, 2004, RES PREPARATION PROP, P57
[5] Aging in chemically prepared divalent silver oxide electrodes for silver/zinc reserve batteries
Smith, DF
Brown, C
[J]. JOURNAL OF POWER SOURCES, 2001, 96 (01) : 121 - 127
[6] Waterhouse Geoffrey I N, 2007, POLYHEDRON, V26, P3310
[7] Wu Yuehui, 2002, JIANGXI CHEM IND, P8
[8] [肖雪松 Xiao Xuesong], 2005, [华东理工大学学报. 自然科学版, Journal of East China University of Science and Technoloy. Natural Sciences Edition], V31, P620
[9] Yang Hui, 2002, CHIN CERAM SOC, V30, P588
[10] Zhang Y., 2007, SYNTHESIS NANOAGO IT, P22

← 1 2 →