A method for testing the interface toughness of ceramic environmental barrier coatings (EBCs) on ceramic matrix composites (CMCs)

A simple interface fracture test for ceramic environmental barrier coatings (EBCs) on ceramic matrix composites (CMCs) was developed. A variation on the asymmetric double cantilever beam (ADCB) test was proposed so that the interface toughness could be measured in a small specimen of simple shape without applying interlaminar loading to the CMC substrate. The proposed test was applied to an EBC consisting of a mullite layer and Si bond coat on a monolithic SiC substrate. A pre-crack was introduced by pop-in cracking, and then a notch overlapping the pre-crack was machined. The pre-crack was opened by inserting a wedge into the notch. From the critical notch opening displacement the crack starts to propagate, interface toughness is calculated. The measured interface toughness was 4.1 J/m2. Finally, the application range of the test was discussed and suggestions were made for introduction of the notch and pre-crack.