ROLE OF CAVITY FORMATION ON CRACK GROWTH OF COLD-WORKED CARBON STEEL, TT 690 AND MA 600 IN HIGH TEMPERATURE WATER

被引：0
|
作者：
Arioka, Koji [1 ]
Miyamoto, Tomoki [2 ]
Yamada, Takuyo [1 ]
Terachi, Takumi [1 ]
机构：
[1] Inst Nucl Safety Syst Inc, 64 Sata, Mihama, Fukui 9191205, Japan
[2] Kobe Mat Testing Lab Co Ltd, Hyogo 6750155, Japan
来源：
15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS | 2011年
关键词：
Cavity formation; IGSCC; Creep; TT690; MA600; Carbon steel; STRESS-CORROSION CRACKING; REACTOR PRESSURE-VESSEL; LOW-ALLOY STEELS; ALPHA-IRON; ENHANCED DIFFUSION; OXYGENATED WATER; SCALE GROWTH; HYDROGEN; VACANCIES; SUSCEPTIBILITY;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The role of cavity formation on crack growth of intergranular stress corrosion cracking (IGSCC) in high temperature water and creep cracking was examined in quantitatively for cold worked carbon steel (ASTM A106 (UNS K03006, CW carbon steel), Alloy 690 (UNSN06690, CW TT 690), and Alloy 600 (UNSN06600, CW MA 600). Three important patterns were observed: First, cavities were observed at grain boundaries just ahead crack tips and crack wall after tests in gas and high temperature water for all test materials. Second, population of cavities decreased with distance from crack tips and crack wall. This result seems to suggest that cavities will form at high stress region such as crack tips before crack advance as crack embryos. Third, good correlation was observed between the rate of cavity formation and crack growth of IGSCC and intergranular creep cracking not only carbon steel, but also TT690 and MA600. Finally, the formation of crack embryos from the collapse of vacancies induced by cold work and absorbed hydrogen play an important role on the process of crack growth both of SCC and creep for CW carbon steel, CW TT690, and CW MA600 in high temperature water.
引用
收藏
页码：55 / 69
页数：15
相关论文
共 50 条
  • [1] Role of Cavity Formation in Crack Initiation of Cold-Worked Carbon Steel in High-Temperature Water
    Arioka, Koji
    Miyamoto, Tomoki
    Yamada, Takuyo
    Aoki, Masanori
    CORROSION, 2013, 69 (05) : 487 - 496
  • [2] Formation of Cavities Prior to Crack Initiation and Growth on Cold-Worked Carbon Steel in High-Temperature Water
    Arioka, K.
    Miyamoto, T.
    Yamada, T.
    Terachi, T.
    CORROSION, 2010, 66 (01)
  • [3] ENVIRONMENTALLY ASSISTED CRACK GROWTH IN COLD WORKED ALLOY 690TT IN PRIMARY WATER AT LOW AND HIGH TEMPERATURES
    Peng, Qunjia
    Shoji, Tetsuo
    Hou, Juan
    Takeda, Yoichi
    Yonezawa, Toshio
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 149 - 158
  • [4] Environmentally assisted crack growth in one-dimensionally cold worked Alloy 690TT in primary water
    Peng, Q. J.
    Hou, J.
    Yonezawa, T.
    Shoji, T.
    Zhang, Z. M.
    Huang, F.
    Han, E. -H.
    Ke, W.
    CORROSION SCIENCE, 2012, 57 : 81 - 88
  • [5] RESISTANCE TO FATIGUE CRACK GROWTH OF COLD WORKED STAINLESS STEEL AT HIGH TEMPERATURE
    SHAHINIAN, P
    SMITH, HH
    WATSON, HE
    REPORT OF NRL PROGRESS, 1971, (JUL): : 21 - +
  • [6] Crack growth testing on Cold Worked Alloy 690 in Primary Water Environment
    Tice, David R.
    Medway, Stuart L.
    Platts, Norman
    Stairmand, John W.
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 71 - 87
  • [7] Dependence of stress corrosion cracking for cold-worked stainless steel on temperature and potential, and role of diffusion of vacancies at crack tips
    Arioka, K.
    Yamada, T.
    Terachi, T.
    Miyamoto, T.
    CORROSION, 2008, 64 (09) : 691 - 706
  • [8] Stages of austenitization of cold-worked low-carbon steel in intercritical temperature range
    Panov, D. O.
    Simonov, Y. N.
    Spivak, L. V.
    Smirnov, A. I.
    PHYSICS OF METALS AND METALLOGRAPHY, 2015, 116 (08): : 802 - 809
  • [9] Stages of austenitization of cold-worked low-carbon steel in intercritical temperature range
    D. O. Panov
    Y. N. Simonov
    L. V. Spivak
    A. I. Smirnov
    The Physics of Metals and Metallography, 2015, 116 : 802 - 809
  • [10] APPLICATION OF J-INTEGRAL PARAMETER TO HIGH-TEMPERATURE FATIGUE CRACK GROWTH IN COLD-WORKED TYPE 316 STAINLESS-STEEL
    SADANANDA, K
    SHAHINIAN, P
    INTERNATIONAL JOURNAL OF FRACTURE, 1979, 15 (02) : R81 - R84
12345