Preparation and characterization of carboxylic-containing poly(methyl methacrylate) nanolatexes

Poly(methyl methacrylate) (PMMA)-based latex particles bearing carboxylic groups at the surface were prepared via emulsion polymerization. The polymerization recipe and process were optimized in order to target monodisperse particles with diameters around 100 nm. The polymerizations were performed using 4,4'-azobis(4-cyanopentanoic) acid (ACPA) as initiator and sodium dodecyl sulphate (SDS) as surfactant. The polymerization conversion was determined by both gas chromatography and gravimetry. The final latexes were characterized with respect to particle size, size distribution, surface charge density, electrokinetic properties (i.e. electrophoretic mobility vs pH and ionic strength) and colloidal stability (i.e. coagulation rate constants vs pH and stability factor vs ionic strength).