Wear Behaviour of Nanostructured Polymer-Based Safety Films on Soda-Lime Glass

被引：3

作者：

Panagopoulos, C. N. ^{[1
]}

Georgiou, E. P. ^{[2
,3
]}

Tradas, G. S. ^{[1
]}

Gianakopoulos, K. I. ^{[1
]}

机构：

[1] Natl Tech Univ Athens, Met Phys Lab, Athens 15780, Greece

[2] Katholieke Univ Leuven KU Leuven, Dept Mat Engn MTM, Kasteelpk Arenberg 44, B-3001 Leuven, Belgium

[3] Falex Tribol NV, Wingepk 23B, B-3110 Rotselaar, Belgium

来源：

COATINGS | 2016年 / 6卷 / 03期

关键词：

glass; multilayered polymeric coatings; safety films; wear; adhesion; ABRASIVE WEAR; BOROSILICATE GLASS; COATINGS; FRICTION; STEEL; COMPOSITES; EROSION;

D O I：

10.3390/coatings6030026

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The wear behaviour of bare and polymer-coated soda-lime glass specimens sliding against 440C stainless steel counterfaces was investigated with the aid of a pin-on-disk apparatus. The selected polymeric coatings were commercially supplied safety films, which are nowadays extensively applied on glass in the automotive and construction industry. One of their main failures is the degradation of their properties due to wear. In this work, the frictional behaviour of these coatings on glass were evaluated and compared to those of bare soda-lime glass. Correlations have been also made between the worn surfaces and weight loss in order to investigate the effect of wear conditions (speed, load) on the wear behaviour of these tribosystems. In addition, during the dry wear of soda-lime glass sliding against stainless steel counterfaces, the dominant wear mechanisms were found to be localized adhesion and abrasion, whereas, in the case of the multilayered polymeric coatings localized adhesion, deformation and tearing were observed.

引用

页数：10

共 50 条

[1] Erratum: Panagopoulos, C.N., et al. Wear Behaviour of Nanostructured Polymer-Based Safety Films on Soda-Lime Glass (vol 6, 26, 2016)
Panagopoulos, N.
Georgiou, E. P.
Tradas, G. S.
Giannakopoulos, K. I.
COATINGS, 2016, 6 (04):
[2] The role of test conditions on the microabrasive wear behaviour of soda-lime glass
Shipway, PH
WEAR, 1999, 233 : 191 - 199
[3] Progressive tool wear in diamond cutting of glass soda-lime
Jia, P.
Zhouland, M.
Huang, S.N.
Key Engineering Materials, 2012, 499 : 138 - 143
[4] The analysis of soda-lime glass
Lundell, GEF
Knowles, HB
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1927, 10 (11) : 829 - 849
[5] HYDRATION OF SODA-LIME GLASS
LANFORD, WA
DAVIS, K
LAMARCHE, P
LAURSEN, T
GROLEAU, R
DOREMUS, RH
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1979, 33 (02) : 249 - 266
[6] KIIIC OF SODA-LIME GLASS
CHEN, CP
LEIPOLD, MH
AMERICAN CERAMIC SOCIETY BULLETIN, 1981, 60 (03): : 373 - 373
[7] Iron oxide coating films in soda-lime glass by triboadhesion
J. O. Aguilar
J. M. Rodríguez-Lelis
M. J. Arjona
Journal of Mechanical Science and Technology, 2009, 23 : 1169 - 1174
[8] Iron oxide coating films in soda-lime glass by triboadhesion
Aguilar, J. O.
Rodriguez-Lelis, J. M.
Arjona, M. J.
JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY, 2009, 23 (04) : 1169 - 1174
[9] Lithographic fabrication of soda-lime glass based microfluidics
Rojas, L.
Norarat, R.
Napari, M.
Kivisto, H.
Chienthavorn, O.
Whitlow, H. J.
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2013, 306 : 296 - 298
[10] Etching of nanostructures on soda-lime glass
Wang, Elmer
Zhao, Yang
OPTICS LETTERS, 2014, 39 (13) : 3748 - 3751

← 1 2 3 4 5 →