Transport properties of multilayered MgB2/Mg2Si superconducting thin film

Electronic transport measurements have been carried out on superconducting MgB2/Mg2Si multilayer film, using a standard four-probe method in perpendicular and parallel applied fields. The film, which was prepared by pulsed-laser deposition, has a layered structure with each MgB2 layer being 40-50 nm thick and the Mg2Si interlayers about 5 nm thick. The flux flow activation energy is deduced from the resistivity-temperature curves using an Arrhenius fit. The results show a clearly enhanced anisotropy of the vortex activation energy in the multilayered film. The irreversibility field and the vortex activation energy are significantly increased in parallel fields. (C) 2006 American Institute of Physics.