Mechanical properties of nanocrystalline L12-type (Al+12.5 at.%M)3Zr (M=Cu, Mn) synthesized by mechanical alloying

被引：0
|
作者：
Lee, SH [1 ]
Moon, KI [1 ]
Lee, KS [1 ]
机构：
[1] Korea Adv Inst Sci & Technol, Dept Mat Sci & Engn, Taejon 305701, South Korea
来源：
Metastable, Mechanically Alloyed and Nanocrystalline Materials | 2005年 / 24-25卷
关键词：
nanocrystalline; intermetallics; fracture toughness;
D O I：
10.4028/www.scientific.net/JMNM.24-25.137
中图分类号：
O7 [晶体学];
学科分类号：
0702 ; 070205 ; 0703 ; 080501 ;
摘要：
Nanocrystalline L1(2)-type (Al + 12.5 at.% M)(3)Zr (M=Cu, Mn) alloys with gain sizes of 8 to 10 nm were prepared by MA and SPS. The micro-hardness was measured to be as high as 975.8 Hv and 983.9 Hv for Cu- and Mn- added alloys, respectively. However, their fracture toughness was below 2 MPam(1/2). The result may indicate that a grain refinement towards the nano scale dose not have a beneficial effect on improving fracture toughness in brittle intermetallics. In this study, some attempts have been made to investigate the effects of grain size on the fracture toughness and the results are presented and discussed.
引用
收藏
页码：137 / 140
页数：4
相关论文
共 50 条
  • [1] Enhancement of the fracture toughness of bulk L12-based (Al+12.5 at. % M)3Zr (M = Cu, Mn) intermetallics synthesized by mechanical alloying
    Lee, SH
    Moon, KI
    Lee, KS
    [J]. INTERMETALLICS, 2006, 14 (01) : 1 - 8
  • [2] Oxidation of (Al+12.5%CU)3Zr intermetallics synthesized by mechanical alloying
    Lee, DB
    Jang, YD
    Kim, SJ
    [J]. DESIGNING, PROCESSING AND PROPERTIES OF ADVANCED ENGINEERING MATERIALS, PTS 1 AND 2, 2004, 449-4 : 821 - 824
  • [3] Microstructural and mechanical properties of nanocrystalline (Al+12.5 at.%Cu)3Zr alloys synthesized by planetary ball milling and spark plasma sintering
    Lee, SH
    Moon, KI
    Hong, HS
    Lee, KS
    [J]. INTERMETALLICS, 2003, 11 (10) : 1039 - 1045
  • [4] A study on the microstructure of D023 Al3Zr and L12 (Al+12.5 at. % Cu)3Zr intermetallic compounds synthesized by PBM and SPS
    Moon, KI
    Kim, SC
    Lee, KS
    [J]. INTERMETALLICS, 2002, 10 (02) : 185 - 194
  • [5] Consolidation behavior of L12 phase (Al+12.5 at. %Cu)3Zr powder with nanocrystalline structure during CIP and subsequent sintering
    Moon, KI
    Hong, HS
    Hong, KT
    Lee, KS
    Kim, SJ
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 380 (1-2): : 46 - 51
  • [6] Thermal stability and mechanical properties of nanocrystalline L12 Al3Hf and (Al+12.5 at.%Zn)3Hf prepared by MA and SPS
    Kang, CW
    Jang, HS
    Kim, SJ
    [J]. DESIGNING, PROCESSING AND PROPERTIES OF ADVANCED ENGINEERING MATERIALS, PTS 1 AND 2, 2004, 449-4 : 809 - 812
  • [7] Hydriding properties of nanocrystalline Mg2-xMxNi alloys synthesized by mechanical alloying (M = Mn, Al)
    Gasiorowski, A.
    Iwasieczko, W.
    Skoryna, D.
    Drulis, H.
    Jurczyk, M.
    [J]. Journal of Alloys and Compounds, 1600, 364 (1-2): : 283 - 288
  • [8] Hydriding properties of nanocrystalline Mg2-xMxNi alloys synthesized by mechanical alloying (M = Mn, Al)
    Gasiorowski, A
    Iwasieczko, W
    Skoryna, D
    Drulis, H
    Jurczyk, M
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 364 (1-2) : 283 - 288
  • [9] SYNTHESIS OF METASTABLE L1(2) CUBIC PHASE IN (AL, M)3ZR (M=FE, NI) POWDERS BY MECHANICAL ALLOYING
    SURYANARAYANA, C
    LI, WK
    FROES, FH
    [J]. SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (11): : 1465 - 1470
  • [10] Synthesis of nanocrystalline L12-Al3Ti and Al3Zr by mechanical alloying
    Nayak, SS
    Murty, BS
    [J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2003, 56 (05) : 457 - 463
12345