The interaction of carbon with Mo5Si3 and W5Si3 suicides. Nowotny phase synthesis

被引：19

作者：

Gnesin, B. A. ^{[1
]}

Gnesin, I. B. ^{[1
]}

Nekrasov, A. N. ^{[2
]}

机构：

[1] ISSP RAS, Chernogolovka 142432, Moscow District, Russia

[2] IEM RAS, Chernogolovka 142432, Moscow District, Russia

来源：

INTERMETALLICS | 2013年 / 41卷

关键词：

Molybdenum silicides; Multiphase intermetallics; Phase identification; Casting; Sintering; Microstructure; MECHANICAL-PROPERTIES; MO-LESS-THAN-OR-EQUAL-TO-5SI3C-LESS-THAN-OR-EQUAL-TO-1;

D O I：

10.1016/j.intermet.2013.04.019

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

High-temperatures reactions of Mo5Si3 and W5Si3 suicides powders with the carbon soot were studied experimentally on sintered and melt-quenched samples. It was shown that Nowotny phase Ma(48)Si(3)C(0.6) may be synthesized after annealing at 1600-2000 degrees C of initial mixture of Mo5Si3 with the carbon soot compacted at room temperature, simultaneously the small quantity of Mo2C phase was synthesized also. We have not found the Nowotny phase for W (like W4.8Si3C0.6) after reactions of W5Si3 or W5Si3 + WSi2 eutectic powders mixtures with carbon neither for the solid state reactions, nor for the melt-quenched samples. Only in some experiments with quenching of melted on the graphite substrate W5Si3 and WSi2 silicides eutectic there were found some evidences of the phase like W4.8Si3C0.6 possible presence along with W5Si3 and WSi2 silicides and WC carbide. In the melt-quenched Mo5Si3 + C sample Nowotny phase for Mo was distinguished from the Mo5Si3 phase in the back-scattered electron image, Mo2C carbides were revealed also. (C) 2013 Elsevier Ltd. All rights reserved.

引用

页码：82 / 95

页数：14

共 50 条

[1] THE CRYSTAL STRUCTURE OF MO5SI3 AND W5SI3
ARONSSON, B
[J]. ACTA CHEMICA SCANDINAVICA, 1955, 9 (07): : 1107 - 1110
[2] Synthesis of the Nowotny phase Mo4.8Si3C0.6 from Mo5Si3 + carbon mixtures
B. A. Gnesin
I. B. Gnesin
[J]. Inorganic Materials, 2015, 51 : 991 - 998
[3] Synthesis of the Nowotny phase Mo4.8Si3C0.6 from Mo5Si3 + carbon mixtures
Gnesin, B. A.
Gnesin, I. B.
[J]. INORGANIC MATERIALS, 2015, 51 (10) : 991 - 998
[4] High-temperature silicon diffusivities in Mo5Si3 and W5Si3 phases
Kharatyan, SL
Chatilyan, HA
Harutyunyan, AB
[J]. DIFFUSIONS IN MATERIALS: DIMAT2000, PTS 1 & 2, 2001, 194-1 : 1557 - 1562
[5] THE FORMATION OF THE PHASE W5SI3
OBROWSKI, W
[J]. JOURNAL OF THE INSTITUTE OF METALS, 1960, 89 (02): : 79 - 80
[6] Formation of Mo5Si3 phase in Mo/Si multilayers
Srivastava, AK
Tripathi, P
Nayak, M
Lodha, GS
Nandedkar, RV
[J]. JOURNAL OF APPLIED PHYSICS, 2002, 92 (09) : 5119 - 5126
[7] ELECTROTRANSFER OF SI IN MO5SI3
KRIVORUCHKO, VM
[J]. INORGANIC MATERIALS, 1979, 15 (07): : 953 - 955
[8] PREPARATION AND CHARACTERIZATION OF MO3SI AND MO5SI3
CHRISTENSEN, AN
[J]. ACTA CHEMICA SCANDINAVICA SERIES A-PHYSICAL AND INORGANIC CHEMISTRY, 1983, 37 (06): : 519 - 522
[9] Combustion Synthesis of Mo5Si3 in Chemical Furnace
Gao, J. -Y.
Jiang, W.
[J]. INTERNATIONAL JOURNAL OF SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS, 2008, 17 (01) : 49 - 53
[10] Combustion synthesis of Mo5Si3 in chemical furnace
J. -Y. Gao
W. Jiang
[J]. International Journal of Self-Propagating High-Temperature Synthesis, 2008, 17 (1) : 49 - 53

← 1 2 3 4 5 →