Application of an Extended Stress-Based Forming Limit Curve to Predict Necking in Stretch Flange Forming

An extension of the stress-based forming limit curve (FLC) advanced by Stoughton (2000, "A General Forming Limit Criterion for Sheet Metal Forming," Int. J. Mech. Sci., 42, pp. 1-27) is presented in this work. With the as-received strain-based FLCs and stress-strain curves for 1.6-mm-thick AA5754 and 1-mm-thick AA5182 aluminum alloy, stress-based FLCs are obtained. These curves are then transformed into extended stress-based forming limit curves (XSFLCs), which consist of the invariants, effective stress, and mean stress. By way of application, stretch flange forming of these aluminum alloy sheets is considered. The AA5754 stretch flange displays a circumferential crack during failure, whereas the AA5182 stretch flange Jails through a radial crack at the edge of the cutout. It is shown that the necking predictions obtained using the strain- and stress-based FLCs in conjunction with shell element computations are inconsistent when compared with the experimental results. By comparing the results of the shell element computations with those in which the mesh comprises eight-noded solid elements, it is demonstrated that the plane stress approximation is not valid. The XSFLC is then used with results from the solid-element computations to predict the punch depths at the onset of necking. Furthermore, it is shown that the predictions of failure location and failure mode obtained using the XSFLC are it? accord with the differences observed between the two alloys/gauges.