Evaluation of mechanical properties of Polyamide 6(PA6) filled with wollastonite and inorganic modified wollastonite

被引：4
|
作者：
Wang, Caili [1 ]
Zheng, Shuilin [2 ]
Wang, Huaifa [1 ]
机构：
[1] Tai Yuan Univ Technol, Coll Min Technol, Taiyuan 030024, Peoples R China
[2] China Univ Min & Technol, Sch Chem & Environm Engn, Beijing 100083, Peoples R China
来源：
ADVANCED MATERIALS AND PROCESS TECHNOLOGY, PTS 1-3 | 2012年 / 217-219卷
关键词：
mechanical properties; PA6; wollastonite; inorganic modified wollastonite; IN-SITU POLYMERIZATION; NANOCOMPOSITES; COMPOSITES; MORPHOLOGY;
D O I：
10.4028/www.scientific.net/AMM.217-219.522
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Some novel composites were prepared with polyamide 6(PA6) filled with wollastonite particles and wollastonite inorganic modified by aluminium silicate composite materials (WIMS) as fibrous fillers. Subsequently, these composites were investigated for tensile, charpy notched impact, bending strength, bending modulus and heat distortion temperature, and the mechanism of PA6 reinforced by WIMS was discussed through SEM photos of wollastonite and WIMS and the current two most popular equations: Pukanszky equation and Nielsen equation. The results show that the PA6 products filled with WIMS have superior mechanical properties(tensile strength 71.65Mpa, bending strength 106.61Mpa, bending modulus 3258.22Mpa) than that of uncoated wollastonite and pure PA6, and the heat distortion temperature increases by 88.6 degrees C than pure PA6 and 17.2 degrees C than wollastonite. Inorganic modification of wollastonite can improve the joint interface between wollastonite and PA6, thus improving their mechanical properties.
引用
收藏
页码：522 / +
页数：2
相关论文
共 50 条
  • [1] Properties of Talc/Wollastonite/Polyamide 6 Hybrid Composites
    Kodal, M.
    Erturk, S.
    Sanli, S.
    Ozkoc, G.
    [J]. POLYMER COMPOSITES, 2015, 36 (04) : 739 - 746
  • [2] Preparation and mechanism of fire retarded PA6/PP/wollastonite composite
    Liu, C.S.
    Wang, Q.
    Xia, H.S.
    [J]. Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering, 2001, 17 (03):
  • [3] Evaluation of mechanical properties of polypropylene filled with wollastonite and silicon rubber
    Singh, Upinder Pal
    Biswas, Bidyut Kumar
    Ray, Bidhan Chandra
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 501 (1-2): : 94 - 98
  • [4] Polyamide fibers (PA6) with antibacterial properties
    Technical Univ of Lodz, Lodz, Poland
    [J]. J Appl Polym Sci, 3 (567-576):
  • [5] Polyamide fibers (PA6) with antibacterial properties
    Buchenska, J
    [J]. JOURNAL OF APPLIED POLYMER SCIENCE, 1996, 61 (03) : 567 - 576
  • [6] POLYAMIDE 6/WOLLASTONITE COMPOSITES - STRENGTH PROPERTIES AND THEIR DEPENDENCE ON HUMIDITY AND TEMPERATURE
    JARVELA, P
    LEBELL, JC
    SANDELIN, B
    JARVELA, P
    TORMALA, P
    [J]. JOURNAL OF MATERIALS SCIENCE, 1986, 21 (12) : 4193 - 4198
  • [7] The mechanical and tribological properties of CF/PPS composite filled with PA6
    Jian, Li
    Tao, Sun
    [J]. JOURNAL OF THERMOPLASTIC COMPOSITE MATERIALS, 2014, 27 (05) : 594 - 602
  • [8] Mechanical properties of polyamide 6 (pa6)/ethylene vinyl acetate (eva)/sepiolite composite
    Fauzi, Noora'tiqah Mohamad
    Mohamad, Zurina
    [J]. MECHANICAL AND MATERIALS ENGINEERING, 2014, 554 : 62 - 65
  • [9] Comparison of the Morphological, Mechanical, and UV Protection Properties of TiO2/Polyamide 6 (PA6), and ZnO/PA6 Nanocomposite Multifilament Yarns
    Ghaffari, Somayeh
    Mojtahedi, M. R. M.
    Dastjerdi, Roya
    [J]. JOURNAL OF MACROMOLECULAR SCIENCE PART B-PHYSICS, 2015, 54 (07): : 783 - 798
  • [10] PREPARATION OF WOLLASTONITE COATED WITH NANO-ALUMINIUM SILICATE AND ITS APPLICATION IN FILLING PA6
    Wang, Caili
    Zheng, Shuilin
    Liu, Guihua
    Wang, Lijing
    Huang, Peng
    Wang, Zhaohua
    [J]. SURFACE REVIEW AND LETTERS, 2010, 17 (02) : 265 - 270
12345