Synthesis and sintering of rare-earth-doped ceria powder by the oxalate coprecipitation method

Doped ceria, which has a higher oxygen ion conductivity than yttria-stabilized zirconia, is one of the possible electrolytes for solid oxide fuel cell at low temperatures. This study concerns powder preparation and densification of rare-earth-doped ceria. Rare-earth-doped ceria powders with a composition of Ce0.8R0.2O1.9 (R = Yb, Y, Gd, Sm, Nd, and La) were prepared by heating the oxalate coprecipitate when a mixed rare earth/cerium nitrate solution was added to an oxalic solution. The oxalate and derived-oxide powders were characterized by x-ray diffraction (XRD), thermogravimetry differential thermal analysis (TG-DTA), particle size analyzer with laser diffraction, inductively coupled plasma (ICP), transmission electron microscopy (TEM), and scanning electron microscopy (SEM). This method provided the oxalate solid solutions containing Ce and R, which were calcined to form the oxide solid solutions at 600 degrees C in air. The lattice parameter of oxide powders increased linearly with increasing ionic radius of doped rare earth. The size of platelike particles of oxalates and oxides depended on the concentration of oxalic acid and showed a minimum at 0.4 M oxalic acid. Dry milling of oxide powder with alpha-Al2O3 ball was effective in reducing the size and aspect ratios of particles with little contamination of Al2O3. These rare-earth-doped ceria powders with various sizes were formed by uniaxial pressing (49 MPa) followed by cold isostatic pressing (294 MPa), and sintered at 900-1600 degrees C in air for 4 h. The micrometer-sized-doped CeO2 powders were densified above 95% of the theoretical density at 1200 degrees C, The grain size of rare-earth-doped ceria after sintering at 1600 degrees C was larger in the samples with the larger rare-earth element.