Conducting film-forming composites based on polyaniline-polyimide blends

A procedure is developed for preparing conducting films by their casting from polymer solutions containing polyaniline in the form of a protonated emeraldin base and polyimides in two cosolvents, N-methylpyrrolidone or m-cresol. Self-supporting films cast from composites based on polyimides and camphorsulfonic acid-protonated polyaniline combine a conductivity of 10(-1)-10(-2)S/cm with good mechanical properties: elastic modulus E = 2.0-2.4 GPa, breaking strength sigma(b) = 55-60 MPa, and elongation at break E >(b) = 8-10%. It has been shown that, when m-cresol and N-methylpyrrolidone are used as cosolvents, the maximum film conductivity is achieved at polyaniline amounts in the composites of 20 and 3%, respectively. In the latter case, films with good strength parameters are formed.