Polypyrrole-Coated Conductive Cotton Prepared by Laccase

被引：4
|
作者：
Zhang, Ying [1 ]
Fan, Xuerong [1 ]
Wang, Qiang [1 ]
机构：
[1] Jiangnan Univ, Minist Educ, Key Lab Sci & Technol Ecotext, Wuxi 214122, Jiangsu, Peoples R China
来源：
JOURNAL OF NATURAL FIBERS | 2018年 / 15卷 / 01期
关键词：
conductive cotton; fabric characterization; fabric modification; in situ polymerization; laccase; pyrrole; POLYANILINE; POLYMERIZATION; ELECTRODE; FABRICS;
D O I：
10.1080/15440478.2017.1302387
中图分类号：
TB3 [工程材料学]; TS1 [纺织工业、染整工业];
学科分类号：
0805 ; 080502 ; 0821 ;
摘要：
Conductive cotton fabric was prepared using laccase as catalytic agent, pyrrole as electric monomer and paratoluene sulfonic acid sodium salt as dopant. The electric resistance of the prepared conductive cotton fabric was 1.22 x 10(7) Omega compared to 3.11 x 10(11) Omega of the original cotton fabric. The abrasion test indicated that polypyrrole was well integrated with the cotton fibers. The conductive cotton fabric also had good antistatic performance and good UV shield capability at 280-400 nm compared to the original cotton fabric. Moreover, the coating of polypyrrole improved the thermo-decomposition behavior of cotton fabrics. Nevertheless, the prepared conductive cotton fabric preserved the same breaking strength as the original cotton fabrics. Compared with original cotton, conductive cotton showed lower gas permeability.
引用
收藏
页码：21 / 28
页数：8
相关论文
共 50 条
  • [1] Polypyrrole-coated conductive paper prepared by vapour-phase deposition method
    Qian, Xueren
    Chen, Jinghuan
    An, Xianhui
    [J]. APPITA JOURNAL, 2010, 63 (02): : 102 - 107
  • [2] Electrical properties of conductive polypyrrole-coated textiles
    Lian, AQ
    Dao, LH
    Zhang, Z
    King, MW
    Guidoin, RG
    [J]. POLYMERS & POLYMER COMPOSITES, 2000, 8 (01): : 1 - 9
  • [3] Electrical properties of conductive polypyrrole-coated textiles
    Lian, Anqing
    Dao, Le H.
    Zhang, Ze
    King, Martin W.
    Guidoin, Robert G.
    [J]. Polymers and Polymer Composites, 2000, 8 (01) : 1 - 9
  • [4] Enhancement in electrical conductive property of polypyrrole-coated cotton fabrics using cationic surfactant
    Lu, Ming
    Xie, Ruyi
    Liu, Zulan
    Zhao, Zhenyun
    Xu, Hong
    Mao, Zhiping
    [J]. JOURNAL OF APPLIED POLYMER SCIENCE, 2016, 133 (32)
  • [5] Development of polypyrrole-coated cotton thermoelectric fabrics
    Jangra, Vivek
    Vishnoi, Prashant
    Maity, Subhankar
    [J]. JOURNAL OF THE TEXTILE INSTITUTE, 2024, 115 (08) : 1287 - 1298
  • [6] FURTHER UNDERSTANDING ON THE CONDUCTIVITY OF POLYPYRROLE-COATED CONDUCTIVE PAPER
    Lei, Yu
    Qian, Xueren
    An, Xianhui
    [J]. 16TH INTERNATIONAL SYMPOSIUM ON WOOD, FIBER AND PULPING CHEMISTRY, PROCEEDINGS, VOLS I & II, 2011, : 1384 - 1388
  • [7] Polypyrrole-coated conductive fabrics as a candidate for strain sensors
    Li, Y
    Leung, MY
    Tao, XM
    Cheng, XY
    Tsang, J
    Yuen, CWM
    [J]. JOURNAL OF MATERIALS SCIENCE, 2005, 40 (15) : 4093 - 4095
  • [8] Polypyrrole-coated conductive fabrics as a candidate for strain sensors
    Y. Li
    M. Y. Leung
    X. M. Tao
    X. Y. Cheng
    J. Tsang
    M. C. W. Yuen
    [J]. Journal of Materials Science, 2005, 40 : 4093 - 4095
  • [9] Polypyrrole-coated cotton fabrics for flexible supercapacitor electrodes prepared using CuO nanoparticles as template
    Xu, Jie
    Wang, Daxiang
    Yuan, Ye
    Wei, Wei
    Gu, Shaojin
    Liu, Ruina
    Wang, Xiaojun
    Liu, Li
    Xu, Weilin
    [J]. CELLULOSE, 2015, 22 (02) : 1355 - 1363
  • [10] Polypyrrole-coated cotton fabrics for flexible supercapacitor electrodes prepared using CuO nanoparticles as template
    Jie Xu
    Daxiang Wang
    Ye Yuan
    Wei Wei
    Shaojin Gu
    Ruina Liu
    Xiaojun Wang
    Li Liu
    Weilin Xu
    [J]. Cellulose, 2015, 22 : 1355 - 1363
12345