Microstructure and Properties of Rapidly Solidified Cu-0.81Cr-0.12Zr Alloy

被引：10
|
作者：
Pan, Zhenya [1 ]
Chen, Jiangbiao [1 ]
Zhou, Wei [1 ]
Li, Jinfu [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, State Key Lab Met Matrix Composites, Shanghai 200240, Peoples R China
来源：
MATERIALS TRANSACTIONS | 2013年 / 54卷 / 08期
基金：
中国国家自然科学基金;
关键词：
copper-chromium-zirconium alloy; rapid solidification; aging; microstructure; properties; CR-ZR ALLOY; CU-CR; COPPER-ALLOYS; MECHANICAL-PROPERTIES; HEAT-TREATMENTS; PRECIPITATION; COMPONENTS; PARTICLES;
D O I：
10.2320/matertrans.M2013107
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Cu-0.81 mass%Cr-0.12 mass%Zr alloy was spun into ribbon and then aged at different temperatures for different time. The microstructure, microhardness and electrical conductivity were investigated. It is found that the mother alloy ingot solidified under conventional conditions consists of three phases: Cu matrix, Cr and Cu5Zr. Rapid quenching makes Cr and Zr fully dissolve into the copper matrix. As the aging proceeds, Cr and Cu5Zr phases precipitate again from the matrix. The ribbon aged at 773 K for 15 min possesses the best property: a microhardness of 212HV and an electrical conductivity of 78.9% IACS. Compared with the conventional process (homogenization treatment of a bulk alloy ingot followed by aging), the use of rapid quenching doubles the microhardness while only slightly decreasing the electrical conductivity.
引用
收藏
页码：1403 / 1407
页数：5
相关论文
共 50 条
  • [1] Microstructure and properties of Cu-Cr-Zr alloy after rapidly solidified, aging and solid solution aging
    Liu, P
    Su, JH
    Dong, QM
    Li, HJ
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2005, 21 (04) : 475 - 478
  • [2] Microstructure and Properties of Cu-Cr-Zr Alloy after Rapidly Solidified Aging and Solid Solution Aging
    Ping LIU
    Journal of Materials Science & Technology, 2005, (04) : 475 - 478
  • [3] Effect of Cr-content and aging on microstructure and properties of the rapidly solidified Cu-Cr-0.05Zr alloys
    Ding, Houfu
    Jinshu Rechuli Xuebao/Transactions of Metal Heat Treatment, 1994, 15 (02):
  • [4] Microstructure and properties of a Cu-Cr-Zr alloy
    Batra, IS
    Dey, GK
    Kulkarni, UD
    Banerjee, S
    JOURNAL OF NUCLEAR MATERIALS, 2001, 299 (02) : 91 - 100
  • [5] Aging precipitation and recrystallization of rapidly solidified Cu-Cr-Zr-Mg alloy
    Zhongguo Youse Jinshu Xuebao, 2 (241-246):
  • [6] Microstructure and properties of aging Cu–Cr–Zr alloy
    Kun Wang
    Ke-Fu Liu
    Jing-Bo Zhang
    Rare Metals, 2014, 33 (02) : 134 - 138
  • [7] Microstructure and properties of aging Cu–Cr–Zr alloy
    Kun Wang
    Ke-Fu Liu
    Jing-Bo Zhang
    Rare Metals, 2014, 33 : 134 - 138
  • [8] Aging precipitation and recrystallization of rapidly solidified Cu-Cr-Zr-Mg alloy
    Liu, P
    Kang, BX
    Cao, XG
    Huang, JL
    Yen, B
    Gu, HC
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 265 (1-2): : 262 - 267
  • [9] Effect of Zr and Mg on the aging precipitation of rapidly solidified Cu-Cr alloy
    Liu, Ping
    Kang, Buxi
    Cao, Xingguo
    Huang, Jinliang
    Gu, Haicheng
    Jinshu Rechuli Xuebao/Transactions of Metal Heat Treatment, 1999, 20 (02): : 46 - 50
  • [10] Interaction of precipitation and recrystallization in rapidly solidified Cu-Cr-Zr-Mg alloy
    Liu, P.
    Kang, B.X.
    Cao, X.G.
    Huang, J.L.
    Yin, B.
    Gu, H.C.
    Acta Metallurgica Sinica (English Letters), 1999, 12 (03): : 273 - 277
12345