Oxidation behavior of Cr-Al-N-O thin films prepared by pulsed laser deposition

被引：25
|
作者：
Hirai, M [1 ]
Saito, H [1 ]
Suzuki, T [1 ]
Suematsu, H [1 ]
Jiang, WH [1 ]
Yatsui, K [1 ]
机构：
[1] Nagaoka Univ Technol, Extreme Energy Dens Res Inst, Nagaoka, Niigata 9402188, Japan
来源：
THIN SOLID FILMS | 2002年 / 407卷 / 1-2期
关键词：
chromium aluminum oxynitride; coatings; NaCl structure; oxidation;
D O I：
10.1016/S0040-6090(02)00024-X
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Chromium aluminum oxynitride (Cr-Al-N-O) films have been successfully prepared by pulsed laser deposition (PLD). Experiments were carried out by changing the surface area ratio of the target [SR = S-AlN/(S-Cr2N+S-AlN)] under a pressure of 1 x 10(-5) torr. The composition of the film prepared at fluence of F = 5 J/cm(2) and Si-R = 75% was determined to be Cr0.11Al0.39N0.25O0.25 by Rutherford backscattering spectroscopy (RBS). The oxidation of the Cr-Al-N-O film was observed above 900 degreesC. Additionally, the film heat-treated at 1100 degreesC consisted mainly of B1 (NaCl) structure. From the result of grazing angle X-ray difftactometry (GXRD), the oxidation resistant of Cr-Al-N-O film was found to be improved due to the fact that Cr2O3 and alpha-Al2O3 is formed near the film surface. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：122 / 125
页数：4
相关论文
共 50 条
  • [1] Characteristics of Cr-Al-N-O thin films prepared by pulsed laser deposition
    Hirai, M
    Saito, H
    Suzuki, T
    Suematsu, H
    Jiang, WH
    Yatsui, K
    BEAMS 2002, 2002, 650 : 445 - 448
  • [2] Characteristics of Cr-Al-N-O thin films prepared by pulsed laser deposition
    Hirai, M
    Saito, H
    Suzuki, T
    Suematsu, H
    Jiang, WH
    Yatsui, K
    SURFACE ENGINEERING 2001 - FUNDAMENTALS AND APPLICATIONS, 2001, 697 : 255 - 260
  • [3] Mechanism of hardening in Cr-Al-N-O thin films prepared by pulsed laser deposition
    Hirai, M
    Suzuki, T
    Suematsu, H
    Jiang, W
    Yatsui, K
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2003, 21 (04): : 947 - 954
  • [4] Preparation of Compositionally Gradient Cr-Al-N-O Thin Films by Pulsed Laser Deposition
    Suzuki, Tsuneo
    Fujinoki, Kazuya
    Asami, Hiroki
    Hirai, Makoto
    Yunogami, Takashi
    Suematsu, Hisayuki
    Yatsui, Kiyoshi
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2012, 76 (06) : 391 - 396
  • [5] Hardness optimization of (Cr,Mg)(N,O) thin films prepared by pulsed laser deposition
    Asami, H.
    Inoue, J.
    Hirai, M.
    Suzuki, T.
    Nakayama, T.
    Suematsu, H.
    Jiang, W.
    Niihara, K.
    AICAM 2005, 2006, 11-12 : 311 - +
  • [6] Characteristics of Cr-Al-N films prepared by pulsed laser deposition
    Suzuki, T
    Hirai, M
    Suematsu, H
    Jiang, W
    Yatsui, K
    PPPS-2001: PULSED POWER PLASMA SCIENCE 2001, VOLS I AND II, DIGEST OF TECHNICAL PAPERS, 2001, : 1838 - 1841
  • [7] Magnetron sputtering of hard Cr-Al-N-O thin films
    Stueber, M.
    Albers, U.
    Leiste, H.
    Seemann, K.
    Ziebert, C.
    Ulrich, S.
    SURFACE & COATINGS TECHNOLOGY, 2008, 203 (5-7): : 661 - 665
  • [8] A tetragonal phase in Cr(N,O) thin film prepared by pulsed laser deposition
    Inoue, Jun
    Nakayama, Tadachika
    Suzuki, Tsuneo
    Suematsu, Hisayuki
    Jiang, Weihua
    Niihara, Koichi
    ECO-MATERIALS PROCESSING & DESIGN VII, 2006, 510-511 : 1006 - 1009
  • [9] Preparation of Cr-Cu-N-O thin films by pulsed laser deposition
    Asami, Hiroki
    Kamekawa, Takayuki
    Suzuki, Tsuneo
    Nakayama, Tadatika
    Suematu, Hisayuki
    Jiang, Weihua
    Niihara, Koich
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2007, 71 (09) : 704 - 707
  • [10] Influence of oxygen content on structure and hardness of Cr-N-O thin films prepared by pulsed laser deposition
    Suzuki, Tsuneo
    Inoue, Jun
    Saito, Hajime
    Hirai, Makoto
    Suematsu, Hisayuki
    Jiang, Weihua
    Yatsui, Kiyoshi
    THIN SOLID FILMS, 2006, 515 (04) : 2161 - 2166
12345